摘要
针对 4114工号不锈钢管道的开裂 ,进行原因分析 ,认为应力腐蚀和选材不当是主要原因。根据工况条件选用了新的钢材并采用了相应的措施 。
This article analyzes the causes of the stainless steel pipe cracking. The main reasons were stress corrosion and using unsuitable materials. According to the operation condition, selecting new proper materials and adoping other acceptable methods have got satisfactory results.
出处
《腐蚀与防护》
CAS
2002年第2期76-78,共3页
Corrosion & Protection