摘要
采用溶胶-凝胶结合低温(<100℃)热水后处理法,在塑料衬底上制得N-Fe共掺杂锐钛矿TiO_2-SiO_2复合薄膜。采用多种技术手段对薄膜样品进行了表征,并考察了薄膜样品在可见光下对罗丹明B的降解能力。研究结果表明,有机衬底上形成了锐钛矿TiO_2纳米晶弥散分布的复合薄膜,薄膜具有较高的可见光催化效率,150min后对罗丹明B的降解效率达到77.4%,其中矿化率达61%。
N-Fe co-doped anatase TiO2-SiO2 composite films were synthesized through sol-gel method followed by hot-water treatment at a low temperature(<100℃) on plastic substrates. The as-prepared samples were first characterized conventionally. The photocatalytic performance was evaluated by the degradation of Rhodamine B(RhB) under visible light. TiO2 nanocrystals were found to disperse uniformly in the composite films, showing highly efficient visible-light-induced photodegradation activity(77.4% @ 150 min) of RhB with a highmineralization efficiency(61% @ 150 min).
作者
卜彦强
马德伟
宋琨
曹鸿涛
吴爱国
王立平
陈亮
金亦君
徐裕
张莉
梁凌燕
张洪亮
高俊华
诸葛飞
BU Yanqiang;MA Dewei;SONG Kun;CAO Hongtao;WU Aiguo;WANG Liping;CHEN Liang;JIN Yijun;XU Yu;ZHANG Li;LIANG Lingyan;ZHANG Hongliang;GAO Junhua;ZHUGE Fei(College of Science,Zhejiang University of Technology,Hangzhou 310014,China;Ningbo Institute of Materials Technology and Engineering,Chinese Academy of Sciences,Ningbo 315201,China;Zhejiang Jinyuan Optoelectronics Co.,Ltd., Ningbo 315500,China;Temasek Laboratories @ NTU,Nanyang Technological University,50 Nanyang Drive 637553,Singapore)
出处
《材料科学与工程学报》
CAS
CSCD
北大核心
2018年第6期921-926,共6页
Journal of Materials Science and Engineering
基金
国家自然科学基金资助项目(51702336和61674156)
浙江省自然科学基金资助项目(LR15F040002)