Creep rupture behavior and microstructural evolution of modified 9Cr-1Mo heat-resistant steel 被引量:3

原文传递
导出
摘要 High-temperature creep rupture behavior of modified 9Cr-lMo steel used for steam cooler was investigated at temperature of 838 and 923 K and stress ranging from 100 to 250 MPa.Based on the analysis of creep rate-time curves,it is found that the creep rupture life decreases with the increase in the applied stress and temperature.The creep damage tolerance factor has been identified as a value of 8.In the normalized and tempered condition,the studied steel shows typical martensitic microstructure with Cr-rich M23C6 and Nb-or V-rich MX precipitates.Moreover,the Laves phase has been found along the grain boundaries.The fracture morphology characterized by field emission scanning electron microscope is adopted to reveal the creep failure mechanisms.The investigated results indicate the occurrence of the transgranular fracture under all the creep test conditions.
出处 《Journal of Iron and Steel Research(International)》 SCIE EI CAS CSCD 2018年第12期1303-1310,共8页 钢铁研究学报(英文版)
基金 National Natural Science Foundation of China (Grant No.51705316) Shanghai Municipal Bureau of Quality and Technical Supervision (No.2016-40).
  • 相关文献

同被引文献20

引证文献3

二级引证文献5

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部