摘要
Sodium ion capacitors(SICs) have been considered as a kind of promising devices to achieve both high power and energy density. However, it is still a challenge to achieve high energy output at elevated power delivery due to the poor rate capability of battery-type electrode materials and the kinetic mismatch with capacitor-type electrode materials. In this work, to fabricate SICs, P2-Na_(0.67)Co_(0.5)Mn_(0.5)O_2(P2-NCM)was chosen as the battery-type cathode material, and a typical metal-organic framework(MOF) material,zeolitic imidazolate framework-8(ZIF-8) derived carbon(ZDC) was utilized as the capacitor-type anode material. Due to the kinetic match and high-rate performance of both electrodes, the ZDC//P2-NCM SICs exhibited an energy output of 18.8 Wh kg^(-1) at a high power delivery of 12.75 kW kg^(-1).
Sodium ion capacitors(SICs) have been considered as a kind of promising devices to achieve both high power and energy density. However, it is still a challenge to achieve high energy output at elevated power delivery due to the poor rate capability of battery-type electrode materials and the kinetic mismatch with capacitor-type electrode materials. In this work, to fabricate SICs, P2-Na_(0.67)Co_(0.5)Mn_(0.5)O_2(P2-NCM)was chosen as the battery-type cathode material, and a typical metal-organic framework(MOF) material,zeolitic imidazolate framework-8(ZIF-8) derived carbon(ZDC) was utilized as the capacitor-type anode material. Due to the kinetic match and high-rate performance of both electrodes, the ZDC//P2-NCM SICs exhibited an energy output of 18.8 Wh kg^(-1) at a high power delivery of 12.75 kW kg^(-1).
基金
supported by Tianjin Municipal Science and Technology Commission (16PTSYJC00010 and 17JCZDJC37100)
the National Natural Science Foundation of China (21773126)