摘要
We report the results of magnetic, thermodynamic, transport and magnetocaloric effect (MCE) studies of newly synthesized Gd_(10)Co_(20)Si_(70) alloy. These measurements confirm an antiferromagnetic transition at T_N=9 K. Both MCE and magnetoresistance (MR) show quadratic dependence on the applied magnetic field, indicating the presence of spin fluctuations in the alloy. The maximum values of the magnetic entropy change determined from the isothermal magnetization data for magnetic field change of 7 and9 T are found to be 10.5 and 15.6 J/kg·K, respectively. As a consequence of the spin fluctuations effect, the MCE peaks are pulled towards high temperature side as asymmetrically broadened peak. The MR attains a large positive value of 73%at 2 K in 8 T. The large MR and reversible MCE make this alloy an attractive multifunctional magnetic material.
We report the results of magnetic, thermodynamic, transport and magnetocaloric effect(MCE) studies of newly synthesized Gd_(10)Co_(20)Si_(7 O) alloy. These measurements confirm an antiferromagnetic transition at T_N=9 K. Both MCE and magneto resistance(MR) show quadratic dependence on the applied magnetic field, indicating the presence of spin fluctuations in the alloy. The maximum values of the magnetic entropy change determined from the isothermal magnetization data for magnetic field change of 7 and9 T are found to be 10.5 and 15.6 J/kg·K, respectively. As a consequence of the spin fluctuations effect, the MCE peaks are pulled towards high temperature side as asymmetrically broadened peak. The MR attains a large positive value of 73% at 2 K in 8 T. The large MR and reversible MCE make this alloy an attractive multifunctional magnetic material.
基金
supported by the result of the Project implementation:University Science Park TECHNICOM for Innovation Applications Supported by Knowledge Technology(ITMS:26220220182)
by the Research&Development Operational Programme funded by the ERDF and VEGA1/0956/17,VEGA 1/0611/18 and APVV-16-0079