API P105油管钢在含CO_2溶液中的电化学腐蚀行为 被引量:2

Influence of NaC1 on Corrosion Behavior of API P105 Steel in CO_2 Saturated Solution
下载PDF
导出
摘要 用电化学阻抗谱(EIS)和极化测量,研究了在含CO2的溶液中NaCl含量对API P105钢 的电化学腐蚀行为的影响.结果表明,随着NaCl含量的增大,P105钢的腐蚀电位正移,抑制了 腐蚀过程的阴阳极反应,降低了P105钢的腐蚀速率.分析表明,Cl-在APIP105钢表面的吸附为 Temkin等温吸附. The effect of NaCJ on the corrosion behavior of API P105 steel in the C02-saturated solution was studied by electrochemical impedance spectrum(EIS) and polarization measurement. The results showed the increase of NaCl concentration decreased the the corrosion rate of the steel, which could be attribulted the decrease of hydroxide ion concentration and the dissolution of C02, and the adsorption of Cl- obeyed the Tem- kin isotherm.
出处 《北京科技大学学报》 EI CAS CSCD 北大核心 2002年第2期197-199,共3页 Journal of University of Science and Technology Beijing
基金 国家自然科学基金资助课题(No.50171011)
关键词 API P105油管钢 含CO2溶液 电化学 腐蚀行为 二氧化碳 electrochemistry corrosion of metal API P105 steel CO2 saturated solution,
  • 相关文献

参考文献5

二级参考文献12

  • 1曹楚南.混合电位下的法拉第导纳[J].中国腐蚀与防护学报,1993,13(2):91-100. 被引量:19
  • 2董俊华,曹楚南,林海潮.酸度和氯离子浓度对工业纯铁腐蚀的促进作用机制研究[J].腐蚀科学与防护技术,1995,7(4):293-299. 被引量:15
  • 3曹楚南.-[J].腐蚀电化学,1994,:140-144.
  • 4毕新民 曹楚南 等.-[J].中国腐蚀与防护学报,1983,3(4):199-199.
  • 5张学元 王凤平 等.-[J].中国腐蚀与防护学报,1999,19(4):311-311.
  • 6曹楚南.-[J].中国腐蚀与防护学报,1985,5(3):156-156.
  • 7曹楚南,中国腐蚀与防护学报,1985年,5卷,3期,155页
  • 8曹楚南,腐蚀电化学原理,1985年,105页
  • 9张学元,中国腐蚀与防护学报,1999年,19卷,4期,311页
  • 10曹楚南,腐蚀电化学,1994年,9页

共引文献133

同被引文献59

  • 1吕拴录,赵国仙,王新虎,严密林,付道明,张建新.特殊螺纹接头油管腐蚀原因分析[J].腐蚀与防护,2005,26(4):179-181. 被引量:38
  • 2张国安,路民旭,吴荫顺.CO_2腐蚀产物膜的微观形貌和结构特征[J].材料研究学报,2005,19(5):537-548. 被引量:44
  • 3Schmitt G. Fundamental Aspects of CO2 Corrosion[A]. In: Hausler R H, Giddard H P, eds. Advances in CO2 Corrosion[C]. Houston, Texas: NACE, 1984, 1:10
  • 4Kermani M B, Morshed A. Carbon dioxide corrosion in oil and gas production - A compendium[J]. Corrosion, 2003, 59(8): 659- 683
  • 5路民旭.高温高压CO2多相介质腐蚀研究及应用的新进展[A].第四届全国腐蚀大会论文集[C].北京:中国腐蚀与防护学会,2003:40-57
  • 6Crolet J L, Bonies M R. A tentative method for predicting the corrosivity of wells in new CO2 fields [A]. Corrosion/85 [C]. Boston, Massachusetts: NACE. 1985, 27
  • 7Dugstad A, Hemmer H, Seiersten M. Effect of steel microstructure upon corrosion rate and protective iron carbonate film formation [A]. Corrosion/2000[C]. Houston, Texas: NACE,2000, 24
  • 8Gulbrandsen E, Nyborg R. Effect of steel microstructure and composition on inhibition of CO2 corrosion [A]. Corrosion/2000 [C]. Houston, Texas: NACE,2000, 23
  • 9Gulbrandsen E, Nesic S, Stangeland A, et al. Effect of precorrosion on the performance of inhibitors for CO2 corrosion of carbon steel[A]. Corrosion/98[C]. Houston Texas: NACE, 1998, 13
  • 10Mora-Mendoza J L, Turgoose S. Fe3C influence on the corrosion rate of mild steel in aqueous CO2 systems under turbulent flow conditions[J]. Corros. Sci., 2002, 44(6): 1223-1246

引证文献2

二级引证文献26

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部