等通道转角挤压纯铝的组织结构 被引量:22

MICROSTRUCTURE OF PURE ALUMINUM WORKED BY EQUAL CHANNEL ANGULAR EXTRUSION
下载PDF
导出
摘要 研究等通道转角挤压方法挤压纯铝的组织结构。纯铝试样经过ECAE挤压 ,在通道转角处产生大的剪切塑性变形 ,使晶粒细化。ECAE前原始晶粒尺寸为 2 μm ,一次挤压后晶粒尺寸约为 1 2 μm ,多次挤压后晶粒不断细化 ,8次后尺寸达到0 .3 μm。同时 ,纯铝随挤压道次增加硬度提高 ,但挤压 3~ 4次后硬度趋于饱和。ECAE技术不仅能够控制晶粒尺度 。 The microstructure of pure aluminum extruded by equal channel angular extrusion (ECAE) is investigated. The grain size of pure aluminum is decreased with the increase of ECAE times because of the large plastic shear deformation. The initial grain size is about 2μm and it becomes to about 1.2μm for one passage and 0.3μm for 8 passages.The hardness of pure aluminum is raised as extrusion times increase in four passages, while extrusion time is more than 4, it is not obvious to fine grain. The grain size and properties of materials can be improved by ECAE.
机构地区 天津理工学院
出处 《有色金属》 CSCD 2002年第2期8-11,共4页 Nonferrous Metals
基金 天津市高校科技发展基金资助项目 (990 3 0 8)
关键词 等通道转角挤压 纯铝 组织结构 亚晶 equal channel angular extrusion pure aluminum sub micron grain
  • 相关文献

参考文献1

  • 1李强.高纯铝和铝合金等通道转角挤压引起的微观组织变化:学位论文[M].中国科学院金属研究所,2000.74.

同被引文献235

引证文献22

二级引证文献108

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部