预防冲模提前失效的对策
被引量:1
Precautionary measure for failure of punching die ahead of its lifetime
摘要
针对长期以来国内冲模寿命偏低的实际情况 ,通过对大量永久失效冲模的剖析 ,介绍冲模的失效形式 ,提出预防冲模提前失效的对策。
出处
《现代制造工程》
CSCD
北大核心
2002年第7期35-37,共3页
Modern Manufacturing Engineering
同被引文献33
-
1平板正人,邢奇源.粘模的各种因素及防止措施[J].模具技术,1989(2):12-18. 被引量:6
-
2E Schedin. Galling mechanisms in sheet forming operations. Wear, 1994. 179,123-128
-
3D M Fabijanic, M Barnett, P D Hodgson, et al. Improving the galling resistance of automotive stamping tools. Metal Forming, 2000. (9):641-646
-
4古林忠.板料冲压中的表面损伤情形.塑性と加工,1978.19(1):25~29
-
5M J Alinger,C J Van Tyne. Evolution of the tribological characteristics of several forming die materials.Journal of Materials Processing Technology, 2001. 111,20-24
-
6Schumacher, William J, Tanczyn, et al. Galling and wear resistant steel alloy. United States Patent, 4494988,January 22,1985
-
7Schumacher, William J, Tanczyn, et al. Galling resistant austenitic stainless steel. United States Patent,4146412, March 27,1979
-
8Schumacher, William J, Tanczyn, et al. Galling resistant austenitic stainless steel. United States Patent,4099967, July 11,1978
-
9B Podgornik. Influence of surface roughness and coating type on the galling properties of coated forming tool steel. Surface and Coating Technology, 2004. 184,338-348
-
10J Takadoum, H H Bennani. Influence of substrate roughness and coating thickness on adhesion, friction and wear of TiN films, Surf. Coat. Technol. 1997. 96,272-282
二级引证文献8
-
1罗建东,阮锋.Ni-P电刷镀在拉深不锈钢材料模具上的应用[J].华南理工大学学报(自然科学版),2007,35(12):17-22. 被引量:1
-
2照日格图,侯英岢,赵亦希,于忠奇.模具表面形态演化对冲压件表面损伤的影响[J].上海交通大学学报,2008,42(5):782-785. 被引量:6
-
3侯英岢,张卫刚,于忠奇,林忠钦.高强度钢板成形中零件表面损伤实验[J].上海交通大学学报,2008,42(9):1433-1437. 被引量:3
-
4侯英岢,张卫刚,于忠奇,李淑慧,陈新平.模具硬度对高强度钢板拉毛缺陷的影响规律研究[J].塑性工程学报,2008,15(6):43-47. 被引量:6
-
5冯艳,杨雪峰,林启权,董文正,殷望.高强钢无凸缘方盒拉深粘模位置预测模型研究[J].热加工工艺,2014,43(1):104-108. 被引量:1
-
6韦荣发,孙威,覃亮,黄峥松,唐广杰.汽车钣金拉伤与开裂的形成机理研究[J].模具工业,2019,45(11):62-67.
-
7李奇颖,吴博雅,杨子帅,黎军顽.循环热冲压过程中高热导率模具钢的摩擦磨损行为[J].材料热处理学报,2022,43(1):75-83. 被引量:6
-
8彭帅,朱晖,侯启军,章光昊,王鹏程.冲压成形拉毛机理与控制方法的研究应用[J].模具制造,2023,23(3):19-24.