摘要
通过对某合成氨装置中置锅炉的腐蚀形貌、工作条件的分析 ,阐明了其应力腐蚀开裂的原因 ,并提出预防措施 .
The causes of stress corrosion cracking was expounded by analyzing corrosion profile and working conditions in synthetic ammonia intermediate waste heat boilers, and the protecting measures were given. It should have a practical value in protection from stress corrosion for the same equipment.
出处
《山东大学学报(工学版)》
CAS
2002年第2期185-189,共5页
Journal of Shandong University(Engineering Science)