摘要
The microstructures and crystallization behavior of Ti-47 at% Ni-3 at% Fe shape memory alloy wire under the condition of severe cold drawing at room temperature and different post-deformation annealing processes were intensively investigated using transmission electron microscope（TEM） and differential scanning calorimetry（DSC）. It is indicated that the amorphous phase is dominant in the Ti50Ni47Fe3 wire after the cold drawing of 78 % areal reduction. The critical temperature for recrystalization is determined at about 300 °C. The average grain size grows from 7 up to 125 nm when annealing temperature rises from300 to 500 °C. Post-deformation annealing process exerts significant influence on the crystallization temperature which climbs up with the increase of annealing temperature.
The microstructures and crystallization behavior of Ti-47 at% Ni-3 at% Fe shape memory alloy wire under the condition of severe cold drawing at room temperature and different post-deformation annealing processes were intensively investigated using transmission electron microscope（TEM） and differential scanning calorimetry（DSC）. It is indicated that the amorphous phase is dominant in the Ti50Ni47Fe3 wire after the cold drawing of 78 % areal reduction. The critical temperature for recrystalization is determined at about 300 °C. The average grain size grows from 7 up to 125 nm when annealing temperature rises from300 to 500 °C. Post-deformation annealing process exerts significant influence on the crystallization temperature which climbs up with the increase of annealing temperature.
基金
financially the National Natural Science Foundation of China (Nos. 50835002 and 51105102)
the Industry, Education and Research Projects of the China Aviation Industrial (No. cxy2012BH04)