Vibration fatigue is the main failure mode of compressor blade. Evaluating the vibration stress of blade that leads to cracking is very useful for analysis of vibration fatigue. In this paper, fatigue stress estimation methods by quantitative fractography were studied through experimental blade and in-service first-stage compressor blade in order to evaluate the initiation vibration stress of in-service blade. The analysis process of initiation vibration stress was established. The evaluating result of vibration stress of in-service blade subjected to centrifugal force and bending vibration stress agrees with aero engine test result. It is shown that the evaluation method can not only evaluate the equivalent fatigue stresses of different crack depths but also yield the initiation equivalent fatigue stress.
Vibration fatigue is the main failure mode of compressor blade. Evaluating the vibration stress of blade that leads to cracking is very useful for analysis of vibration fatigue. In this paper, fatigue stress estimation methods by quantitative fractography were studied through experimental blade and in-service first-stage compressor blade in order to evaluate the initiation vibration stress of in-service blade. The analysis process of initiation vibration stress was established. The evaluating result of vibration stress of in-service blade subjected to centrifugal force and bending vibration stress agrees with aero engine test result. It is shown that the evaluation method can not only evaluate the equivalent fatigue stresses of different crack depths but also yield the initiation equivalent fatigue stress.
基金
financially supported by Equipment Advance Research Fund of China (No. 9140A1211HK51)