A novel synthesis of hierarchical porous carbons （HPCs）with 3D open-cell structure based on nanosilica- embedded emulsion-templated polymerization was reported. An oil-in-water emulsion containing SiO2 colloids was fabricated using liquid paraffin as an oil phase, resorcinol/formaldehyde and silica sol as an aqueous phase, and Span 80/Tween 80 as emulsifiers. HPCs with macropore cores, open meso/ macropore windows, and abundant micropores were synthesized by the polymerization and carbonization of the emulsion, followed by scaffold removal and further KOH activation. A typical HPCs sample as supercapacitor electrode shows the charge/discharge capability under large loading current density （30 A/g） coupling with a reasonable electrochemical capacitance in KOH electrolyte solution.
A novel synthesis of hierarchical porous carbons （HPCs）with 3D open-cell structure based on nanosilica- embedded emulsion-templated polymerization was reported. An oil-in-water emulsion containing SiO2 colloids was fabricated using liquid paraffin as an oil phase, resorcinol/formaldehyde and silica sol as an aqueous phase, and Span 80/Tween 80 as emulsifiers. HPCs with macropore cores, open meso/ macropore windows, and abundant micropores were synthesized by the polymerization and carbonization of the emulsion, followed by scaffold removal and further KOH activation. A typical HPCs sample as supercapacitor electrode shows the charge/discharge capability under large loading current density （30 A/g） coupling with a reasonable electrochemical capacitance in KOH electrolyte solution.
基金
supported by the National Natural Science Foundation of China(Nos.21207099 and 21273162)
Science and Technology Commission of Shanghai Municipality,China(Nos. 11nm0501000 and 12ZR1451100)
Key Subject of Shanghai Municipal Education Commission(No.J50102)