摘要
用金相显微组织法研究了SKS51钢在不同工艺条件下的脱碳行为,比较与分析了薄板坯连铸连轧流程与传统流程的脱碳规律,以及热轧SKSS1钢带在不同的加工条件下所发生脱碳的程度以及影响因素.结果表明：高碳钢单面脱碳层深度小于板带厚度的0.5％,为传统流程的30％～60％.
The decarburization characters of steel SKS51 were investigated under different process conditions by means of microstructure comparison technique. The author did research on decarburization when the strip was hot - roiled during the thin slab casting and roiling, compared the different decarburization between the thin slab casting and roiling and traditional process and investigated the decarburization degree and influencing factors when the steel SKS51 was hot -rolled under different processing conditions. The results show that its single face deearburization depth is less than 0.5 %of strip thickness, only 30%- 60%of that traditional process.
出处
《南方金属》
CAS
2014年第4期13-16,共4页
Southern Metals
关键词
CSP工艺
高碳合金工具钢
脱碳
CSP process
high carbon alloy steel
decarburization