SiO_2亚微米颗粒对染料敏化电池光阳极性能的影响

Effect of Sub-micro SiO_2 Particle on the Performance of DSSC Anode
下载PDF
导出
摘要 为了提高染料敏化太阳能电池中光的吸收,在光阳极中掺入湿式研磨法得到的SiO2亚微米颗粒。分别对比掺入前后的散射光谱及染色后光谱吸收情况,实验证明,利用此方法制备的TiO2纳米晶体颗粒薄膜,光散射得到增强,经染色后光的吸收也得到了加强。同时,利用此阳极组装的太阳能电池,电流提高了15%。 In order to improve the light absorption in dye -sensitized solar cells anode ,the SiO2 particles sub-micro are mixed with TiO2 nanocrystal anode ,which is obtained by wet grinding method .Experiments show that ,using TiO2 nanocrystal anode film prepared by this method ,light scattering is enhanced .After dyeing ,light absorption has also been strengthened .At the same time ,by using the anode assembly ,short current can be increased by 15% .
出处 《广东石油化工学院学报》 2014年第4期60-62,共3页 Journal of Guangdong University of Petrochemical Technology
基金 广东石油化工学院实验课题研究项目(201103) 茂名市工农业科技计划项目(201340)
关键词 染料敏化电池 亚微米颗粒 散射中心 Dye-sensitized solar cells Sub-micro particle Scattering center
  • 相关文献

参考文献7

  • 1Gratzel M. Solar energy conversion by dye - sensitized photovohaic cells[ J ]. Inorg. Chem., 2005 ( 44 ) : 6841 - 6851.
  • 2Hore S, Nitz P, Vetter C, et al. Influence of scattering layers on efficiency of dye- sensitized solar cells[ J]. Chem, Commun., 2005,15 (3) :2011 - 2013.
  • 3Halaoui L I, Abrams N M, Mallouk T E. Increasing the conversion efficiency of dye - sensitized TiO2 photo - electrochemical cells by couphng to photonic crystals [ J ]. Phys. Chem. B, 2005 (109) : 6334 - 6342.
  • 4Zhang Qifeng, Chou P T, Bryan Russo, et al. Aggregation of ZnO nanocrystaffites for high conversion efficiency in Dye - sensitized solar cells[ J ]. Angew. Chem. Int. Ed., 2008 ( 47 ): 2402 - 2406.
  • 5王渊喆.染料敏化太阳电池光阳极的光散射增强与光伏性能优化[D].上海:上海师范大学,2013.
  • 6田贵才.微粒子的线度对Mie散射光强度影响的研究[J].原子与分子物理学报,2002,19(3):334-336. 被引量:1
  • 7况琦,杨斌,刘婧.ITO薄膜导电性能对温度的响应[J].浙江理工大学学报(自然科学版),2010,27(5):721-724. 被引量:2

二级参考文献7

  • 1WANGLiduo LIYang CHANGChun DUANLian QIUYong.Research on the adhesive ability between ITO anode and PET substrate improved by polyimide buffer layer[J].Chinese Science Bulletin,2005,50(6):505-508. 被引量:5
  • 2Betz U,Kharrazi M,Marthy J.Thin films engineering of indium tin oxide:large area flat panel displays application[J].Surface and Coatings Technology,2006,200:5751-5759.
  • 3Chopra K L,Major S,Pandya D K.Transparent conductors:a status review[J].Thin Solid Films,1983,102:1-12.
  • 4Kim Yong-nam,Jeong Seong-min,Jeon Min-seok.Reliability assessment of indium tin oxide thin films by accelerated degradation test[J].Electroceram,2006,17:955-958.
  • 5Nomura K,Sakuma J,Ooki T.Mossbauer study on indium tin oxides(ITO) doped with Fe[J].Hyperfine Interact,2008,184:117-121.
  • 6Aden A L, Kerker M.Scattering of electromoynetic waves from two concentric spheres[J]. Joumal of Applied Physics, 1951,22:1 242.
  • 7田贵才.Al_2O_3/C复合微粒子散射强度分布的计算[J].原子与分子物理学报,2001,18(3):269-272. 被引量:13

共引文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部