摘要
针对聚醚复合型抗静电ABS材料在使用过程中存在看与之接触的电源负极铜端子腐蚀的情况,通过电流试验确认了高温和高湿是造成铜端子腐蚀的主要原因,并提出了防止铜端子腐蚀的措施。
In view of corrosion of copper terminal contacted to cathode of current source and when contacted with the polyether composite antistatic ABS materials, through current test, it is confirmed that high temperature and high humidity are the main causes of corrosion of copper terminals, and some measures to prevent copper terminals from corrosion are provided.