A new aluminosilicate long-lasting phosphor with composition of NaA1SiO4：Eu2＋,Ho3＋ was synthesized and investigated. Under UV light excitation, the phosphor emitted yellow light corresponding to the characteristic emission of Eu2＋ due to 5d-4f transi- tion. Bright yellow phosphorescence sustaining for more than 30 rain was observed after ceasing the excitation. The phosphorescence intensity decay obeyed a fl decay law, indicating a tunneling electron-hole recombination process in the phosphor. Four peaks ap- peared in the thermoluminescence curve and the ones at 322 and 370 K were thought to account for the long lasting phosphorescence at room temperature. The Ho3＋ ion incorporated into the phosphor did not give any light but dramatically increased the intensities of both photoluminescence and phosphorescence via promoting defect levels in the phosphor.
A new aluminosilicate long-lasting phosphor with composition of NaA1SiO4：Eu2＋,Ho3＋ was synthesized and investigated. Under UV light excitation, the phosphor emitted yellow light corresponding to the characteristic emission of Eu2＋ due to 5d-4f transi- tion. Bright yellow phosphorescence sustaining for more than 30 rain was observed after ceasing the excitation. The phosphorescence intensity decay obeyed a fl decay law, indicating a tunneling electron-hole recombination process in the phosphor. Four peaks ap- peared in the thermoluminescence curve and the ones at 322 and 370 K were thought to account for the long lasting phosphorescence at room temperature. The Ho3＋ ion incorporated into the phosphor did not give any light but dramatically increased the intensities of both photoluminescence and phosphorescence via promoting defect levels in the phosphor.
基金
Project supported by the Funds for Creative Research Groups of China(21221061)