共混硫化丁腈橡胶-氯丁橡胶的物理性能

Physical properties of blended and vulcanizednitrile-butadiene rubber/chloroprene rubber

将丁腈橡胶(NBR)和氯丁橡胶(CR)按不同质量分数共混并硫化,研究了硫化橡胶在自然环境、热空气老化、热油老化等条件下的物理性能,并测定了硫化橡胶与镀铜钢丝的粘合性能.结果表明,随着CR质量分数的增大,混炼胶的焦烧时间逐渐缩短.经热空气老化后,NBR的硬度增加幅度比CR的硬度增加幅度大,拉断强度降低幅度则比CR的小得多.此外,NBR的耐油性能优于CR.就物理性能以及与镀铜钢丝的粘合性能而言,单一NBR和单一CR优于共混NBR/CR.

Nitrile-butadiene rubber （NBR）and chloroprene rubber （CR）were blended at differ-ent mass fractions and vulcanized,followed by aging at various conditions.The physical prop-erties of the vulcanized rubbers aged at ambient condition as well as in hot air and hot oil were determined,and their adhesion to Cu-coated steel wires was measured as well.Results indicate that,with the increase of the mass fraction of CR,the scorch time of the gross rubber tends to decline gradually.After being aged in hot air,the hardness of vulcanized NBR tends to rise more noticeably than that of vulcanized CR,while the tensile strength of the vulcanized NBR reduces at a much less extent than that of the vulcanized CR.Moreover,vulcanized NBR exhib-its better resistance against oil than vulcanized CR,while mono NBR and mono CR are advan-tageous over blended NBR/CR in terms of the physical properties and adhesion to Cu-coated steel wire.