The influences of Ca and Y additions on the microstructure and corrosion resistance of vacuum die-cast AZ91 alloys were investigated by optical microscope,electron scanning microscope,weight-loss test,and electrochemical corrosion experiment.The results indicate that the Ca or Ca and Y additions refined the microstructure and decreased the amount of Mg17Al12 phase on grain boundaries in the alloys.Meanwhile,the addition of Ca and Y led to the formation of network Al2 Ca phase and rod-like Al2 Y phase,improved the corrosion resistance of AZ91 magnesium alloy.Compared with AZ91 alloy,the corrosion rate of AZ91–1.5Ca–1.0Y alloy was decreased to 16.2%,and its corrosion current density was dropped by one order of magnitude after immersion in 3.5 wt% NaCl solution for 24 h.
The influences of Ca and Y additions on the microstructure and corrosion resistance of vacuum die-cast AZ91 alloys were investigated by optical microscope,electron scanning microscope,weight-loss test,and electrochemical corrosion experiment.The results indicate that the Ca or Ca and Y additions refined the microstructure and decreased the amount of Mg17Al12 phase on grain boundaries in the alloys.Meanwhile,the addition of Ca and Y led to the formation of network Al2 Ca phase and rod-like Al2 Y phase,improved the corrosion resistance of AZ91 magnesium alloy.Compared with AZ91 alloy,the corrosion rate of AZ91–1.5Ca–1.0Y alloy was decreased to 16.2%,and its corrosion current density was dropped by one order of magnitude after immersion in 3.5 wt% NaCl solution for 24 h.