Corrosion Performance of High Strength 15Cr Martensitic Stainless Steel in Severe Environments

Corrosion Performance of High Strength 15Cr Martensitic Stainless Steel in Severe Environments
原文传递
导出
摘要 High pressure and high temperature corrosion performance of high strength 15 Cr martensitic stainless steel was studied in different severe environments—live acid(10%HCl+1.5%HF+3%HAc+5.1% corrosion inhibitor),spent acid and formation water containing CO2.The results show that the corrosion of high strength 15 Cr martensitic stainless steel in live acid is most serious,and the uniform corrosion rate is far greater than those in spent acid and formation water containing CO2 corrosion environments,but all of them can be acceptable for oilfield.Acidizing corrosion inhibitor displays a good matching ability with the high strength 15 Cr martensitic stainless steel in terms of decreasing the uniform corrosion rate,which changes mainly the anodic process of high strength 15 Cr martensitic stainless steel.The corrosion potential moves to the positive direction,thus the corrosion current density decreases significantly.There are some different degrees of pitting of high strength 15 Cr martensitic stainless steel after corrosion tests in live acid,spent acid and formation water containing CO2,and the pitting density aggravates significantly and the maximum pit depth decreases in the corrosion sequence. High pressure and high temperature corrosion performance of high strength 15 Cr martensitic stainless steel was studied in different severe environments—live acid(10%HCl+1.5%HF+3%HAc+5.1% corrosion inhibitor),spent acid and formation water containing CO2.The results show that the corrosion of high strength 15 Cr martensitic stainless steel in live acid is most serious,and the uniform corrosion rate is far greater than those in spent acid and formation water containing CO2 corrosion environments,but all of them can be acceptable for oilfield.Acidizing corrosion inhibitor displays a good matching ability with the high strength 15 Cr martensitic stainless steel in terms of decreasing the uniform corrosion rate,which changes mainly the anodic process of high strength 15 Cr martensitic stainless steel.The corrosion potential moves to the positive direction,thus the corrosion current density decreases significantly.There are some different degrees of pitting of high strength 15 Cr martensitic stainless steel after corrosion tests in live acid,spent acid and formation water containing CO2,and the pitting density aggravates significantly and the maximum pit depth decreases in the corrosion sequence.
出处 《Journal of Iron and Steel Research International》 SCIE EI CAS CSCD 2014年第8期774-780,共7页
基金 Item Sponsored by National Natural Science Foundation of China(51271146,51074126)
关键词 high strength 15Cr martensitic stainless steel live acid spent acid CO2 corrosion high strength 15Cr martensitic stainless steel live acid spent acid CO2 corrosion
  • 相关文献

参考文献12

  • 1J. Boles, M. J. Ke, C. Parker, in: SPE International (Eds. ), The 2009 SPE Annual Technical Conference and Exhibition, Society of Petroleum Engineers Inc., Louisiana, 2009, No. 124887.
  • 2W. Jiang, K. Y. Zhao, D. Ye, J. u, Z. D. Li, J. Su , J. Iron Steel Res. Int. 20 (2013) No.5, 61-65.
  • 3L. C. Wang, M. L. Li, W. Q. Cheng, G. S. Wang, Hydrogeology and Engineering Geology 37 (2010) No.5, 128-132.
  • 4B. Guo, E. A. Hu, R. S. Zhang, Test Methods and Evaluation of Acidizing Corrosion Inhibitor Performance, China, SY IT 5405-1996, 1996.
  • 5NACE International, Preparation, Installation, Analysis, and Interpretation of Corrosion Coupons in Oilfield Operations, NACE SP 0775-2013, USA.
  • 6M. Kimura, K. Sakata, K. Shirnamoto , in: NACE International (Eds. ), 62th NACE Annual Conference, Ornnipress , Houston, 2007, No. 07087.
  • 7S. Ghareba , S. Ornanovic , Corros. Sci. 52 (2010) 2104-2113.
  • 8E. Bayol , T. Gurten , A. Ali Gurten , M. Erbil, Mater. Chern. Phys, 112 (2008) 624-630.
  • 9M. J. Ke, J. Boles, in: SPE International (Eds. ), The 1st International Symposium on Oilfield Corrosion, Society of Petroleum Engineers Inc. , Louisiana, 2004, No. 87561.
  • 10Y. R. Liu , D. Ye, Q. L. Yong, J. Su , K. Y. Zhao, W. Jiang, J. Iron Steel Res. Int. 18 (2011) No. 11, 60-66.

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部