摘要
The basic formulation of Al2O3- C slide plates was65%（ in mass,the same hereinafter） white fused corundum particles,25% white fused corundum fines,6% active α-Al2O3 micropowder,4% carbon black and flake graphite, and additional 4% phenolic resin.Based on this formulation,3% Al powder,3% Si powder,and 3% Al ＋ 3% Si powder were used to substitute equivalent white corundum fines to improve the hot mechanical properties of Al2O3- C slide plates. The specimens with dimensions of 140 mm × 25 mm × 25 mm were pressed at 150 MPa,dried at 200 ℃ for 24 h,and hot treated at 1 400 ℃ for 3 h in carbon embedded condition. Then hot modulus of rupture and thermal shock resistance of the specimens were tested and the phase compositions and microstructure were analyzed. The results show that specimen with 3% Al powder has the higher hot modulus of rupture but lower residual modulus of rupture after thermal shock than the specimen with3% Si powder; the specimen with 3% Al ＋ 3% Si powders exhibits the highest hot modulus of rupture and the best thermal shock resistance; the change of mechanical property is closely related with the in-situ formed nonoxides： AlN in the form of bars is formed in specimens with Al powder; fibrous SiC whiskers are formed in specimens with Si powder; in the specimens with both Al and Sipowders,besides AlN and SiC whiskers,hexagonal tabular SiAlON is in-situ synthesized,which interlocks with each other.
The basic formulation of Al2O3- C slide plates was65%（ in mass,the same hereinafter） white fused corundum particles,25% white fused corundum fines,6% active α-Al2O3 micropowder,4% carbon black and flake graphite, and additional 4% phenolic resin.Based on this formulation,3% Al powder,3% Si powder,and 3% Al ＋ 3% Si powder were used to substitute equivalent white corundum fines to improve the hot mechanical properties of Al2O3- C slide plates. The specimens with dimensions of 140 mm × 25 mm × 25 mm were pressed at 150 MPa,dried at 200 ℃ for 24 h,and hot treated at 1 400 ℃ for 3 h in carbon embedded condition. Then hot modulus of rupture and thermal shock resistance of the specimens were tested and the phase compositions and microstructure were analyzed. The results show that specimen with 3% Al powder has the higher hot modulus of rupture but lower residual modulus of rupture after thermal shock than the specimen with3% Si powder; the specimen with 3% Al ＋ 3% Si powders exhibits the highest hot modulus of rupture and the best thermal shock resistance; the change of mechanical property is closely related with the in-situ formed nonoxides： AlN in the form of bars is formed in specimens with Al powder; fibrous SiC whiskers are formed in specimens with Si powder; in the specimens with both Al and Sipowders,besides AlN and SiC whiskers,hexagonal tabular SiAlON is in-situ synthesized,which interlocks with each other.