对TRIP钢板进行了一系列高周疲劳试验,对800MPa强度级别的TRIP钢的疲劳极限、疲劳寿命系数进行了研究,并与同强度级别的DP钢板进行了对比。分析了TRIP钢疲劳断口的显微组织以及TRIP效应对TRIP钢疲劳性能的影响。结果表明:TRIP效应对钢的疲劳抗力有所贡献,在循环基数为107次下,TRIP钢的疲劳极限值明显高于DP钢,拥有更高的抗疲劳性能,TRIP钢疲劳裂纹源与疲劳区有明显韧性断裂特征。
The high cycle fatigue performance of TRIP automobile steel is investigated. First, a series of high cycle fatigue experiments of TRIP steel were conducted. Then, the fatigue limit and fatigue life factor at 800 MPa tensile strength level were studied, and compared with that of DP steel plate at the same strength level. Finally, the microstructure of the fatigue fracture and influence of TRIP effect on the fatigue property of TRIP steel were analyzed. Results show that the TRIP effect improves the fatigue resistance of the steel to some extent. Under the 107 times cycle base condition, the fatigue limit of TRIP steel is obviously higher than that of DP steel, and its fatigue resistance performance is better. The crack source and fatigue area of TRIP steel show obvious ductile fracture characteristics.
出处
《吉林大学学报（工学版）》
EI
CAS
CSCD
北大核心
2014年第5期1371-1374,共4页
Journal of Jilin University:Engineering and Technology Edition
基金
国家自然科学基金项目(51171030)
关键词
金属材料
TRIP钢
DP钢
断口扫描
疲劳性能
metallic material
TRIP steel
DP steel
fracture scanning
fatigue performance