Tungsten film(W film) is deposited by using the ion beam assisted deposition(IBAD) on the 316 L substrate surface in this experiment. The micro structure and nano-hardness of the film are investigated by scanning electron microscopy(SEM) and nano-indentation tester. The tribological behavior of W film under lubrication by oil with ZDDP and MoDTC is evaluated by a SRV test machine. The tribo-film formed on the worn surfaces is investigated by X-ray photoelectron spectroscopy(XPS) to find out the tribological mechanisms between the W film and the two additional additives. The result shows that the W film lubricated by ZDDP and MoDTC-blended base oil has synergistic effects on the friction reduction property, while the anti-wear property is mainly caused by the hard surface of W film.
Tungsten film (W film) is deposited by using the ion beam assisted deposition (IBAD) on the 316L substrate surfacein this experiment. The micro structure and nano-hardness of the film are investigated by scanning electron microscopy(SEM) and nano-indentation tester. The tribological behavior of W film under lubrication by oil with ZDDP and MoDTCis evaluated by a SRV test machine. The tribo-film formed on the worn surfaces is investigated by X-ray photoelectronspectroscopy (XPS) to find out the tribological mechanisms between the W film and the two additional additives. The resultshows that the W film lubricated by ZDDP and MoDTC-blended base oil has synergistic effects on the friction reductionproperty, while the anti-wear property is mainly caused by the hard surface of W film.
基金
the Beijing Natural Science Foundation (3132023)
the National Natural Science Foundation of China (51275494 and 51005218)
the Fundamental Research Funds for the Central Universities (2652012115 and 2652013081)
the Tribology Science Fund of State Key Laboratory of Tribology (SKLTKF13B10) for their financial support to this research