铁素体不锈钢CMT焊接接头HAZ组织性能研究

Microstructure and Properties of Ferritic Stainless Steel CMT Welding HAZ

针对铁素体不锈钢焊接HAZ晶粒易长大的问题,提出采用小热输入的CMT焊接工艺。通过分析接头HAZ的显微组织、显微硬度和冲击性能,探讨了4003铁素体不锈钢焊接接头HAZ组织和性能,并与常规MIG焊焊接接头试样的组织、性能进行对比。试验结果表明:采用CMT焊接工艺获得的接头HAZ粗晶区宽度为460μm,明显窄于MIG焊接接头的粗晶区宽度545μm;CMT接头强度与MIG焊接接头显微硬度值相近,但CMT接头HAZ冲击韧性较MIG焊接接头试样提高了16.28%。

In this paper ,CM T welding process as a kind of low heat input process was adopted ,aiming at the problem that the ferritic stainless steel HAZ grain is easy to grow up .Contrast to the traditional MIG welding joints ,the CMT welding joints＆#39;appearance ,microstructure ,microhardness and impact property in HAZ were analyzed of the 4003 ferritic stainless steel . The results show that the width of joint coarse grain zone of the CMT welding is 460μm ,which is narrower than the width value 545 μm of MIG welding joint .The microhardness of the CMT welding joint is near to the MIG welding joint ,but the toughness is increased by 16 .28% .