以L2B4O7和LiBO2[,(L2B4O7)∶m(LiBO2)=2∶1 为熔剂,LiNO3为氧化剂,LiBr为脱模剂,熔融法制备样品,建立了X射线荧光光谱对冶金渣料中的TFe、SiO2、TCa、MgO、TiO2、MnO、P2O5、Al2O3、K2O和Na2O的快速检测方法.采用高炉渣、转炉渣、电炉渣系列标样绘制校准曲线,并通过加入钾长石、钠长石等适宜标准样品进行曲线分析范围扩展,使曲线既可以用于高炉渣、转炉渣、电炉渣等炉渣类样品分析,也可用于保护渣样品的检测分析.试验对稀释比、熔样温度、保护渣试样预处理温度等主要条件进行了探讨.结果表明,当试样与熔剂质量比为1∶10和熔样温度为1 050℃(熔样前保护渣样品预处理温度以700℃为宜)时,所得试样在熔剂中分散度(浓度)适当,同时适用于中高、低含量组分的测定.对一标准样品进行10次测定,各组合测定结果的相对标准偏差为0.07%~1.9%.方法用于各类实际冶金渣料分析时,结果与其他分析方法相一致.
A rapid method was developed for the determination of TFe. SiO2, TCa、 MgO、TiO2、 MnO、 P2O5.Al2O3、K2O and Na2O in metallurgical slag by X-ray fluorescence spectrometry (XRF). The sample was prepared by the fused method, using L2 B4 07 and LiBO2 [m (L2 B4O7 ) : m (LiBO2) = 2 : 1] as flux, LiNO3 as oxidizer and LiBr as release agent. A series of standard reference materials of blast furnace slag, converter slag, and electric furnace slag were used for establishing calibration curves. By addition of the reference materials of potassium feldspar and soda feldspar, the test range of curve was extended from slag to mould powder. The main experimental conditions of dilution ratio, fusion tem- perature and pre-treatment temperature were studied. The results showed that, when the mass ratioof sample to flux was chosen as 1 : 10 and the fusion temperature and the pre-treatment temperature of the mould powder were at 1 050℃ and 700℃ respectively, the concentration of the sample in the flux was proved to be suitable for determination of both major and minor contents by XRF. The rela- tive standard deviations (RSDs, n=10) for analysis of a reference material were from 0.07% to 1.9%. The test results were consistent with those of other methods in the determination of actual metallurgi- cal slags.
出处
《冶金分析》
CAS
CSCD
北大核心
2014年第8期39-44,共6页
Metallurgical Analysis
关键词
X射线荧光光谱法
炉渣
保护渣
熔融制样
基体校正
X-ray fluorescence spectrometry
slag
mould powder
fusion sample preparation
matrixcorrection