Influence of silicon on the microstructures, mechanical properties and stretch-flangeability of dual phase steels

Uniaxial tension tests and hole-expansion tests were carried out to determine the influence of silicon on the microstructures, mechanical properties, and stretch-flangeability of conventional dual-phase steels. Compared to 0.03wt% silicon, the addition of 1.08wt% silicon induced the formation of finer ferrite grains （6.8μm ） and a higher carbon content of martensite （Cm≈ 0.32wt%）. AS the silicon level increased, the initial strain-hardening rate （n value） and the uniform elongation increased, whereas the yield strength, yield ratio, and stretch-flangeability decreased. The microstructures were observed after hole-expansion tests. The results showed that low carbon content martensite （Cm ≈ 0.19wt%） can easily deform in coordination with ferrite. The relationship between the mechanical properties and stretch-flangeability indicated that the steel with large post-uniform elongation has good stretch-flangeability due to a closer plastic incom- patibility of the ferrite and martensite phases, which can effectively delay the production and decohesion of microvoids.