The effect of particle shape on the rheological behavior of small particle-large polymer chain mixture solutions has been investigated with two model colloidal silica dispersions, one of which is ellipsoidal（BINDZIL20/440） and the other is spherical（TM40）. It was found that BINDZIL20/440 series showed shear-thickening at lower shear rates and had a lower upper limit in PEO concentration to demonstrate shear-thickening phenomena. The particle shape was identified as the major factor accounting for these differences. This work enables one to control the rheological behavior of colloid-polymer mixture through simply changing particle geometry instead of performing surface modifications, which could be especially useful in cases where only certain chemicals are allowed, for example in vivo applications.
The effect of particle shape on the rheological behavior of small particle-large polymer chain mixture solutions has been investigated with two model colloidal silica dispersions, one of which is ellipsoidal（BINDZIL20/440） and the other is spherical（TM40）. It was found that BINDZIL20/440 series showed shear-thickening at lower shear rates and had a lower upper limit in PEO concentration to demonstrate shear-thickening phenomena. The particle shape was identified as the major factor accounting for these differences. This work enables one to control the rheological behavior of colloid-polymer mixture through simply changing particle geometry instead of performing surface modifications, which could be especially useful in cases where only certain chemicals are allowed, for example in vivo applications.
基金
supported by the Institute of Chemistry,Chinese Academy of Sciences through the"Young Excellence Project",the"Knowledge Innovation Program of the Chinese Academy of Sciences"(No.KJCX2-YW-H19)
National Natural Science Foundation of China(No.91027032)
National Key Technology R&D Program of China(No.2011BAI02B05)
State Key Development Program of Basic Research of China(No.2012CB933200)