摘要
利用扫描电镜对镀锌钢丝扭转试验异常断口进行分析,结果显示,锌铁合金层之间的纵向裂纹以及钢材中的条状硫化物是造成断口异常的原因。
Some galvanizing wires with abnormal torsion fracture are analyzed with the help of the scan-ning electronic microscope .The findings indicates that the abnormal torsion fracture is caused by longitu-dinal cracks between zinc and iron ,long sulfide inclusions in the galvanizing wires .
出处
《武汉工程职业技术学院学报》
2014年第3期34-37,共4页
Journal of Wuhan Engineering Institute
关键词
镀锌钢丝
扭转
异常断口
裂纹
条状硫化物
galvanized wire
torsion
abnormal fracture
crack
long sulfide inclusion