超薄型纯棉织物耐久阻燃整理生产实践 被引量:1

Durable flame retardant finish of light-weight cotton fabric
下载PDF
导出
摘要 针对纯棉织物(单位面积质量160 g/m2以下)的耐久阻燃整理,通过优化阻燃整理液中的配套助剂和阻燃工艺条件,以赋予织物耐久阻燃性能。优化的阻燃整理工艺为:纯棉耐久阻燃剂TEX-1(CP)420 g/L、环保树脂MF 50 g/L、纤维保护剂BH 40 g/L和磷酸(85%)20 g/L;带液率75%,焙烘温度165℃,焙烘时间2.5 min。超薄型纯棉织物经该阻燃整理后阻燃效果佳,耐洗性比较好,且手感柔软。 Durable flame retardant finishing is carried out on cotton fabric of 160 g/m2. The optimum com- bination of auxiliaries in flame retardant solution and flame retardant process are discussed. The opti- mum flame retardant finishing process is as follows: flame retardant TEX-I(or CP) 420 g/L, eco resin MF 50 g/L, fiber protection agent BH 40 g/L, phosphoric acid(g5%) 20 g/L, pickup 75 %, curing at 165 ℃ for 2.5 min. The treated cotton fabric features good flame retardant effect and durability, as well as soft handle.
出处 《印染》 北大核心 2014年第19期30-32,共3页 China Dyeing and Finishing
关键词 阻燃整理 耐久性 棉织物 超薄 flame retardant finish durability cotton fabric ultra light weight
  • 相关文献

参考文献6

二级参考文献32

  • 1邱春阳,张克铮.二氧化硅溶胶稳定性的研究[J].辽宁石油化工大学学报,2005,25(2):1-4. 被引量:38
  • 2程靖环 陶绮雯.染整助剂[M].北京:纺织工业出版社,1990..
  • 3上海市印染工业公司编.印染手册[M].北京:中国纺织出版社,1987.424.
  • 4[1]Price D,Horrocks A R.Akalin M.Influence of flame retardants on the mechanism of pyrolysis of cotton(cellulose)fabrics in air[J].Journal of Analytical and Applied Pyrolysis,1997,40(5):511-524.
  • 5[2]Lecoeur E,Vroman I,Bourbigot S,etal.Flame retardant formulations for cotton[J].Polymer Degradation and Stability,2001,74:487-492.
  • 6[3]Lewin M.Unsolved problems and unanswered questions in flame retardance of polymers[J].Polymer Degradation and Stability,2005,88:13-19.
  • 7[4]Kindley L M,Podall H E,Filipescu N.Novel phosphorus containing polymers[J].Polymers,1962,2(2):122-125.
  • 8[5]Li Q,Jiang P K,Wei P.Synthesis,characteristic,and application of new flame retardant containing phosphorus,nitrogen,and silicon[J].Polymer Engineering and science,2006.46(3):344-350.
  • 9[6]Lecoeur E,·Vroman I,Bourbigot S,etal.Optimization of monoguanidine dihyarogen phosphate and amimo propylethoxysilane based flame retardant formulations for cotton[J].Polymer Degradation and Stability,2006,91:1909-1914.
  • 10[7]LeBlanc B R,Badger H J.Aminoalkylphosphonic acid ester-based textile fire retardants[P].US4013813.1977,3.

共引文献33

同被引文献12

  • 1宁培森,王红梅,丁著明.磷系织物阻燃剂的研究进展[J].精细与专用化学品,2007,15(11):5-9. 被引量:15
  • 2张悦,张迎春,陈丽颖.低甲醛耐久阻燃剂的合成及应用[J].印染.2005,31(9):15-17.
  • 3Bob A. Howell, Adina Dumitrascu. Comparison of the lmpael of Phosphorus and Phosphorus/Nitrogen on the Flammability of Sty- renic Oligomers [J]. Fire and Polymers Vh New Advances in Flame Retardant Chemistry and Science, 2012, 17: 235-250.
  • 4Li Yu-Chin, Schulz Jessica, Mannen Sarah, et al. Flame Retar- dant Behavior of Polyeleetrolyte-Clay Thin Film Assemblies on Cotton FabriclJ]. ACS Nano, 2010, 4(6) :3325-3337.
  • 5Galina Lauir, Christopher Kirkland, Alexander B Morgan, et al. Intumescent Multilayer Nanocoating, Made with Renewable Polyelectrolytes, for Flame-Retardant Cotton [J]. Biomacromole- cules, 2012, 13 (9) : 2843-2848.
  • 6Chen Ming-Jun, Shao Zhu-Bao, Wang Xiu-Li, et al. Halogen- Free Flame-Retardant Flexible Polyurethane Foam with a Novel Nitrogen-Phosphorus Flame Retardant[J]. Ind. Eng. Chem. Res., 2012, 51 (29) :9769-9776.
  • 7刘玉桂,任元林.无卤环保型阻燃环氧树脂的研究进展[J].天津工业大学学报,2011,30(1):74-78. 被引量:4
  • 8房长婧,梁倩倩,龚静华,马敬红,徐坚.磷系阻燃共聚酯纤维的微观结构与性能[J].合成纤维工业,2011,34(2):11-14. 被引量:8
  • 9刘会亮,叶周华,关晋平,蔡建和,周绍强.新型棉用膨胀型阻燃体系[J].印染,2014,40(17):5-7. 被引量:5
  • 10陈朝晖,杜云恒,王则臻,邓启刚,王斐.亚麻织物的含磷阻燃整理[J].印染,2015,41(1):13-16. 被引量:8

引证文献1

二级引证文献2

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部