摘要
以质量分数30%Al2O3-70%SiC为基,外加2%-10%CaO-TiO2 复合烧结助剂,制备了-系列SiC基复相材料. 研究了不同的烧成温度和CaO-TiO2 含量对该复相材料烧结性能的影响.研究结果表明,1400-1500 ℃,随着烧结温度升高,烧结致密性明显提高.烧结温度为1450℃时,试样基本致密.当烧结助剂达到10%(质量分数)时,显气孔率降至0.15%,陶瓷烧结致密.烧结助剂CaO-TiO2,αGAl2O3和方石英反应,在1200 ℃已经生成CaAl2Si2O8,在1300℃以后才开始生成CaTiSiO5,促进6HGSiC进一步氧化.烧结过程中,CaAl2Si2O8 转化为玻璃相,在促进莫来石生成的同时也使试样致密.在1500 ℃,复合材料的主晶相为6HGSiC和莫来石.
6 H-SiC and α-Al2 O 3 powders that as raw materials were mixed as mass ratio of 7 ∶3 with CaO and TiO 2 as sintering additives.The green body was preoxidated for 1 h at 1 200 ℃ after being pressed.Sic matrix composites were prepared by pressureless sintering for 1 h in hydrogen atmosphere.The effects of CaO-TiO 2 content and sintering temperature on the sintering properties and phasecomposition were investigated.The re-sults suggested that:withthe increase of sintering temperature form 1 400 to 1 500 ℃,the compactness im-proves significantly.At the sintering temperature of 1 450 ℃,the samples were basically compact.And the sam-ple's apparent porosity decreased to 0.15% with m (CaO-TiO 2 )of 10% added.The reaction of CaO-TiO 2 cristo-balite,with α-Al2 O 3 ,had generated CaAl2 Si2 O 8 at 1 200 ℃,and generated CaTiSiO 5 after 1 300 ℃,which pro-mote the 6 H-SiC further oxidation.In the process of sintering,CaAl2 Si2 O 8 formed liquid glass phase which de-posits mullite and promoted sample’s densification.At 1 500 ℃,the main crystal phase of the composite materi-al was 6 H-SiC,mullite.
出处
《功能材料》
EI
CAS
CSCD
北大核心
2014年第21期21068-21071,共4页
Journal of Functional Materials
基金
长江学者和创新团队发展计划资助项目(PCSIRT
IRT1146)
关键词
SIC
常压烧结氢气
显气孔率
SiC
pressureless sintering
hydrogen
apparent porosity