摘要
Stainless steel （S S）/carbon steel （C S） clad plates were generated by means of the all-around weld of interface and vacuuming （AAWIV） followed by hot rolling, wherein AAWIV was utilized for controlling the interface oxidation during hot rolling. The structure near the interface was analyzed by optical microscopy （OM）, scanning electron mi- croscopy （SEM） and transmission electron microscopy （TEM）. The mechanical properties of SS/CS clad plates were investigated by tensile and shear as well as bend tests. The SS/CS interface is relatively flat and no visible separation appears. Line scanning analysis shows that diffusion of Cr and Ni from SS to CS and C from CS to SS occurred during bonding. Higher dislocation densities are observed in both layers of parent plates adhering to the interface. The SS/ CS clad plates reveal higher yield, tensile and shear strengths. Both macroscopic delamination at the interface and fracture of base CS as well as intergranular fracture appearance of flyer plate are observed in the tensile test. The shear specimen fails in a ductile manner and the bend specimen tested shows no visible crack at the interface. Taking both interracial structure and mechanical properties into account, the SS/CS clad plates exhibit sound bonding by the process of AAWIV and hot rolling.
Stainless steel （S S）/carbon steel （C S） clad plates were generated by means of the all-around weld of interface and vacuuming （AAWIV） followed by hot rolling, wherein AAWIV was utilized for controlling the interface oxidation during hot rolling. The structure near the interface was analyzed by optical microscopy （OM）, scanning electron mi- croscopy （SEM） and transmission electron microscopy （TEM）. The mechanical properties of SS/CS clad plates were investigated by tensile and shear as well as bend tests. The SS/CS interface is relatively flat and no visible separation appears. Line scanning analysis shows that diffusion of Cr and Ni from SS to CS and C from CS to SS occurred during bonding. Higher dislocation densities are observed in both layers of parent plates adhering to the interface. The SS/ CS clad plates reveal higher yield, tensile and shear strengths. Both macroscopic delamination at the interface and fracture of base CS as well as intergranular fracture appearance of flyer plate are observed in the tensile test. The shear specimen fails in a ductile manner and the bend specimen tested shows no visible crack at the interface. Taking both interracial structure and mechanical properties into account, the SS/CS clad plates exhibit sound bonding by the process of AAWIV and hot rolling.
基金
Item Sponsored by National Key Technology Research and Development Program in 12th Five-year Plan of China(2012CB722801)
National Natural Science Foundation of China(51105264)
Postdoctoral Science Foundation of China(2012M520677)