Effect of H_2 Reduction Temperature on the Properties of Reduced Graphene Oxide and Copper Matrix Composites 被引量:3

Effect of H_2 Reduction Temperature on the Properties of Reduced Graphene Oxide and Copper Matrix Composites
原文传递
导出
摘要 Reduced graphene oxide (RGO) and copper composites (RGO/Cu) were successfully fabricated based on a molecular-level mixing method (MLM). The composite powders were reduced in H2 at 350, 450, and 550℃ and then consolidated by spark plasma sintering (SPS) in order to evaluate the effect of H2 reduction temperature on the properties of the composites. The results indicate that the strengths of the composite decrease with the increase of H2 reduction temperature, while the electrical conductivity reaches its maximum at 450 ℃ and minimum at 550 ℃. Hot rolling could benefit the electrical conductivity. The yield strength of the RGO/Cu composite reduced to 337 MPa at 350℃. The electrical conductivity of the RGO/Cu composite reduced at 450℃ after hot rolling reaches 60.26% IACS. The properties of the RGO/Cu composites can be designed by adjusting the reduction degree of RGO and by hot rolling. Reduced graphene oxide (RGO) and copper composites (RGO/Cu) were successfully fabricated based on a molecular-level mixing method (MLM). The composite powders were reduced in H2 at 350, 450, and 550℃ and then consolidated by spark plasma sintering (SPS) in order to evaluate the effect of H2 reduction temperature on the properties of the composites. The results indicate that the strengths of the composite decrease with the increase of H2 reduction temperature, while the electrical conductivity reaches its maximum at 450 ℃ and minimum at 550 ℃. Hot rolling could benefit the electrical conductivity. The yield strength of the RGO/Cu composite reduced to 337 MPa at 350℃. The electrical conductivity of the RGO/Cu composite reduced at 450℃ after hot rolling reaches 60.26% IACS. The properties of the RGO/Cu composites can be designed by adjusting the reduction degree of RGO and by hot rolling.
出处 《Acta Metallurgica Sinica(English Letters)》 SCIE EI CAS CSCD 2014年第5期924-929,共6页 金属学报(英文版)
基金 financially supported by the National Basic Research Program of China (No.2011CB612200) Program of Qinghai Science and Technology Department (No.2012-Z-701) Harbin Key Technologies R&D Program (No.2012DB2CP029)
关键词 NANOSTRUCTURE COPPER COMPOSITES HYDROGEN Mechanical properties Nanostructure Copper Composites Hydrogen Mechanical properties
  • 相关文献

参考文献20

  • 1K.S. Novoselov, A.K. Geim, S.V. Morozov, D. Jiang, Y. Zhang, S.V. Dubonos, I.V. Grigorieva, A.A. Firsov, Science 306, 666 (2004).
  • 2C. Lee, X.D. Wei, J.W. Kysar, J. Hone, Science 321, 385 (2008).
  • 3J.H. Chen, C. Jang, S.D. Xiao, M. Ishigami, M.S. Fuhrer, Nat. Nanotechnol. 3, 206 (2008).
  • 4A.A. Balandin, S. Ghosh, W.Z. Bao, I. Calizo, D. Teweldebrhan, F. Miao, C.N. Lau, Nano Lett. 8, 902 (2008).
  • 5A.K. Geim, K.S. Novoselov, Nat. Mater. 6, 183 (2007).
  • 6Z. Chen, W.C. Ren, L.B. Gao, B.L. Liu, S.F. Pei, H.M. Cheng, Nat. Mater. 10, 424 (2011).
  • 7M. Qian, Y.S. Zhou, Y. Gao, J.B. Park, T. Feng, S.M. Huang, Z. Sun, L. Jiang, Y.F. Lu, Appl. Phys. Lett. 98, 173108 (2011).
  • 8D.Y. Cai, M. Song, C.X. Xu, Adv. Mater. 20, 1706 (2008).
  • 9M. Wang, S.K. Jang, W.J. Jang, M. Kim, S.Y. Park, S.W. Kim, S.J. Kahng, J.Y. Choi, R.S. Ruoff, Y.J. Song, S. Lee, Adv. Mater. 25, 2746 (2013).
  • 10J. Hwang, M. Kim, V.B. Shields, M.G. Spencer, J. Cryst. Growth 366, 26 (2013).

同被引文献15

引证文献3

二级引证文献6

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部