The transition from vortex glass to a liquid phase is studied in Ba Ni0.1Fe1.9As2 single crystal with Tc = 19.4 K by magneto-resistance measurements. The resistivity curves are measured in magnetic fields in a range of 0 T–13 T for H‖c and H⊥c. Good scalings for all values of resistivity ρ（H, T） and the effective pinning potential U0（H, T） are obtained with the modified vortex glass theory by using the critical exponents s and H0. Phase diagrams for H‖c and H⊥c are determined based on the obtained vortex glass temperature Tg, the vortex dimensionality crossover temperature T＊, and the upper critical magnetic field Hc2. Our results suggest that both below and above 5 T, single vortex pinning co-exists with collective creep, and collective creep is dominant. There is a narrower vortex liquid region for H⊥c than for H‖c in the vortex phase diagram, which may originate from a stronger pinning force.
The transition from vortex glass to a liquid phase is studied in Ba Ni0.1Fe1.9As2 single crystal with Tc = 19.4 K by magneto-resistance measurements. The resistivity curves are measured in magnetic fields in a range of 0 T–13 T for H‖c and H⊥c. Good scalings for all values of resistivity ρ（H, T） and the effective pinning potential U0（H, T） are obtained with the modified vortex glass theory by using the critical exponents s and H0. Phase diagrams for H‖c and H⊥c are determined based on the obtained vortex glass temperature Tg, the vortex dimensionality crossover temperature T＊, and the upper critical magnetic field Hc2. Our results suggest that both below and above 5 T, single vortex pinning co-exists with collective creep, and collective creep is dominant. There is a narrower vortex liquid region for H⊥c than for H‖c in the vortex phase diagram, which may originate from a stronger pinning force.
基金
Project supported by the Foundation of Henan Educational Committee,China(Grant No.13B140951)
the Foundation of Henan University of Technology,China(Grant Nos.11JCYJ15 and 2011BS030)