参照工业上砂加气混凝土工艺,研究水淬锰渣作为硅质材料和轻质骨料制备加气混凝土的可行性,通过对两种加气混凝土进行性能测试及SEM微观观察,研究了其抗压强度、收缩性能和水化产物,并分析了两者性能之间的差异。
Referring to industry technology of sand aerated concrete, the feasibility of water quenching manganese slag used to produce aerated concrete as siliceous material and lightweight aggregates was investigated. Through perfor-mance tests and SEM microanalysis, the differences of compressive strength, shrinkage properties and hydration products between two kinds of aerated concrete are researched and analyzed.
出处
《混凝土与水泥制品》
北大核心
2014年第11期17-20,共4页
China Concrete and Cement Products
基金
广西科技攻关项目(桂科攻12118041-3D)
关键词
水淬锰渣
加气混凝土
抗压强度
水化产物
Water quenching manganese slag
Aerated concrete
Compressive strength
Hydration products