热处理制度对Ti-5Mo-5V-6Cr-3Al钛合金力学性能的影响研究 被引量:1

Effect of Heat Treatment on Mechanical Properties of Ti-5Mo-5V-6Cr-3Al Alloy
下载PDF
导出
摘要 研究了铬含量对Ti-5Mo-5V-3Al-Cr系合金相变点和锻造抗力的影响规律,采用不同的固溶温度、冷却方式和时效处理制度对Ti-5Mo-5V-6Cr-3Al合金显微组织和力学性能的影响进行了研究。结果表明:降低Ti-5Mo-5V-3Al-Cr系合金中的铬含量可以提高相变点和降低锻造抗力。Ti-5Mo-5V-6Cr-3Al合金经800℃×30 min水冷固溶处理后的综合力学性能较热锻后优良;经800℃×30 min水冷+580℃×4 h空冷时效处理后,合金棒材具有优良的综合力学性能,可以作为锻造机加工成品的最终热处理强化工艺,可以满足不同用户对合金的使用要求。 The effects of Cr content on the β transus temperature and stress for Ti-5Mo-5V-3Al-Cr system alloy were studied. The microstructure and mechanical properties of Ti-5Mo-5V-6Cr-3Al alloy were investigated through different solution treatments, cooling methods and aging treatments. The results show that the β transus temperature can be improved and the stress can be decreased by reducing Cr content. The mechanical properties of Ti-5Mo-5V-6Cr-3Al alloy after solution treatment at 800 ℃ for 30 min(WQ) are better than after hot forging. The comprehensive mechanical properties are excellent after heat treatment at 800 ℃ for 30 min(WQ) and then aging at 580 ℃ for 4 h(AC), which can meet the requirement of the alloy for different clients.
出处 《热加工工艺》 CSCD 北大核心 2014年第22期187-189,共3页 Hot Working Technology
基金 陕西省工业科技攻关项目(2012K07-03) 西安市未央区科技计划项目(201312)
关键词 Ti-5Mo-5V-6Cr-3Al合金 固溶处理 时效处理 力学性能 Ti-5Mo-5V-6Cr-3Al alloy solution treatment aging treatment mechanical properties
  • 相关文献

参考文献10

二级参考文献42

共引文献73

同被引文献21

  • 1Qin R S, Wallach E R. Aphase-field model coupled with a thermo- dynamicdatabase[J]. ActaMater. , 2003,51 : 6199-6210.
  • 2Steinbach I, 2:hang L, Plapp M. Phase-field model with finite in- terface dissipation[J]. ActaMater., 2012,60: 2689-2701.
  • 3Zhang L, Steinbach I. Phase-field model with finite interface dissi- pation: Extension to multi-component multi-phase alloys[J]. Acta Mater., 2012,60: 2702-2710.
  • 4Lukas H L, Fries S G, Sundman B. Computational Thermody- namic: The CalphadMethod[M]. New York: Cambridge Univer- sityPress, 2007.
  • 5Hu B, Zhang W W, Peng Y B, et al. Thermodynamic reassess- ment of the AI-Cr-Si system with the refined description of the A1-Cr system[J]. Thermochim. Acta, 2013,561 : 77-90.
  • 6HaoD, HuB, ZhangK, etal. ThequaternaryAl-Fe-Ni-Siphasee- quitibria in Al-rich comer: Experimental measurement and thermo- dynamicmodeling[J]. J. Mater. Sci.,2014,49 : 1157-1169.
  • 7Du Y, Liu S H, Zhang L J, et al. An overview on phase equilibria and thermodynamic modeling in multicomponent A1 alloys: focusing on the A1-Cu-Fe-Mg-Mn-Ni-Si-Zn system [J]. CALPHAD, 2011,35 : 427-445.
  • 8Niessen A K, de Boer F R, Boom R, et al. Model predictions for the enthalpy of formation of transition metal alloys II [J]. CAL- PHAD, 1983,1(1): 51-70.
  • 9Sangster J, Bale C W, Burton B P. in: Phase Diagrams of Binary IronAlloys[M]. Ohio: Materials information Soc. , 1993.
  • 10Bale C W. The Li-Ti (Lithium-Titanium) system [J]. Bull. A1- loyPhaseDiagrams, 1989, 10(2): 135-138.

引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部