种晶介导的二氧化铈球状粒子的形成

Synthesis of Ce02 Spherical-like Particles by Seed-mediated Method
下载PDF
导出
摘要 文章报道了一种以不同数量种晶介导合成CeO2多晶纳米颗粒的制备方法,分析以种晶介导球状的CeO2的形成机理。在生长阶段,CeO2粒子通过初级粒子在其表面的沉积来生长,从而降低了粒子的表面能,导致由许多初级粒子组成的次级粒子的形成。加入的一定量的紧密堆积的种晶聚集体优先作为初级粒子的沉积中心来降低它们的表面能,从而减小次级粒子的尺寸、增加其均匀性以及促进这些次级粒子的形成。 In the paper, a seed-mediated synthesis method for preparation of Ce02 particles with variation of seeds amount was exported, and the formation mechanism was analyzised. During the growth stage, CeO2 particles grew with deposition of the primary nanoparticles other than the monomers to reduce the surface energy of particles, leading to the formation of secondary particles consisting of many primary particles. The densely piled seeds were added and used as the deposition centers of the primary particles formation of these to minimize their surface energy, resulting secondary particles.
出处 《纳米科技》 2014年第5期19-23,共5页
关键词 CeO2粒子 种晶 形成 CeO2 particles seeds formation the decreased size and accelerated
  • 相关文献

参考文献11

  • 1Y. Yamada, C. Tsung, W. Huang, Z. Huo and S. E. Habas. Nanocrystal Bilayer for Tandem Catalysis [J]. Nature Chem istry, 2011, 3, 372-376.
  • 2M. Yamashita, K. K. Kameyama, S. Yabe and S. Yoshida. Synthesis and Microstructure of Calcia Doped Ceria as UV filters [J]. J. Mater. Sci., 2002, 37, 683-687.
  • 3A. Corma and P. Atienzar. Hierarchically Mesostructured Doped CeO2 with Potential for Solar-cell Use [J]. Nature Materials, 2004, 3, 394-397.
  • 4C. R. Stanek, A. H. H. Tan, S. L. Owens and R. W. Grimes. Atomistic Simulation of CeOz Surface Hydroxylation: Implications for Glass Polishing [J]. J. Mater. Sci., 2008, 43, 4157-4162.
  • 5T. Sugimoto, X. P. Zhou and A. Muramatsu. Synthesis of Uniform Anatase TiO2 Nanoparticles by Gel-sol Method: 3. Formation Process and Size Control [J]. J. Colloid Interface Sci., 2003, 259, 43-52.
  • 6T. K. Sau and C. J. Murphy. Room Temperature, High- yield Synthesis of Multiple Shapes of Gold Nanoparticles in Aqueous Solution [J]. J. Am. Chem. Soc., 2004, 126, 8648-8649.
  • 7H. L. Wu, C. H. Kuo and M. H. Huang. Seed-mediated Synthesis of Gold Nanocrystals with Systematic Shape Evolution from Cubic to Trisoctahedral and Rhombic Dodecahedral Structures [J]. Langmuir, 2010, 26, 12307- 12313.
  • 8M. Lin, Z. Y. Fu, H. R. Tan, S. C. Ng and E. Teo. Hydrothermal Synthesis of CeO2 Nanoerystals: Ostwald Ripening or Oriented Attachment [J]. Cryst. Growth Des., 2012, 12 3296-3303.
  • 9D. S. Zhang, F, H. Niu, H. R. Li, L. Y. Shi and J. H. Fang. Uniform Ceria Nanospheres: Solvothermal Synthesis, Formation Mechanism, Size -control and Catalytic Activity [J]. Powder Technology, 2011, 207, 35-41.
  • 10X. S. Zhen, L. Liu, X.P. Zhou. Formation and Properties of Hydrophobie CeO2 Nanoparticles [J]. Colloid Journal, 2014,76(5), 1-7.

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部