The effect of Ce/La misch metal addition on the microstructural evolution of as-cast and as-soluted Mg-5.3Zn-0.5Ca（wt.%） alloys was systematically investigated. It was found that Ce/La could effectively refine the as-cast alloy and restrain grain growth during solution treatment, which was derived from the constitutional supercooling during solidification process and the formation of stable intermetallic compounds Ce Mg12 and Mg17La2. Furthermore, Ce/La microalloying and solution treatment resulted in an evolution from the original lamellar Ca2Mg6Zn3/α-Mg to the divorced eutectic structure. The thermal stability of Mg-Zn-Ca alloy could be effectively improved by Ce/La addition, because the low-melting-point binary Mg-Zn phase was transformed to Mg x Zn y-Ca-（Ce/La） phase with higher thermal stability and the amount of Ca2Mg6Zn3/α-Mg eutectic structure was reduced.
The effect of Ce/La misch metal addition on the microstructural evolution of as-cast and as-soluted Mg-5.3Zn-0.5Ca（wt.%） alloys was systematically investigated. It was found that Ce/La could effectively refine the as-cast alloy and restrain grain growth during solution treatment, which was derived from the constitutional supercooling during solidification process and the formation of stable intermetallic compounds Ce Mg12 and Mg17La2. Furthermore, Ce/La microalloying and solution treatment resulted in an evolution from the original lamellar Ca2Mg6Zn3/α-Mg to the divorced eutectic structure. The thermal stability of Mg-Zn-Ca alloy could be effectively improved by Ce/La addition, because the low-melting-point binary Mg-Zn phase was transformed to Mg x Zn y-Ca-（Ce/La） phase with higher thermal stability and the amount of Ca2Mg6Zn3/α-Mg eutectic structure was reduced.
基金
supported by the National Natural Science Foundation of China(51401200)
Natural Science Foundation of Jilin Province(20140520099JH)
National Science & Technology Pillar Program(2012BAE01B04)
Chinese Academy of Sciences of Western Action Plan Project(KZCX2-XB3-06)
the National Natural Science Foundation of China Major Project(91122030)
National High Technology Research and Development Program of China(2011AA03A407)
National Natural Science Foundation for Creative Research Group(20921002)