苎麻织物阻燃整理工艺

The Flame-retardant Finishing Process of Ramie Fabric

研究了苎麻织物的阻燃整理工艺,分析了阻燃工艺的影响因素和阻燃整理对苎麻织物性能的影响。结果表明,采用阻燃剂用量140g/L,焙烘温度160℃,焙烘时间4min的阻燃工艺,苎麻织物的阻燃效果最好,且耐洗性良好,织物强力的损伤较小。经阻燃整理后织物的透湿性略有下降,但抗皱性有明显的提高。

The flame-retardant finishing process of ramie fabric was studied. The process parameters of flame-retardant finishing of ramie fabric were analyzed, and the influences of the finishing process on the ramie fabric properties were discussed. The result indicated that when the concentration of flame-retardant FR-C was 140 g/L and cured at 160 ℃ for 4 min, the finished ramie fabric exhibited the best flame-retardancy, good durable-washing properties and little damage to breaking strength. The moisture permeability of the finished ramie fabric was decreased slightly, and the wrinkle resistance was increased obviously after flame-retardant finishing.