通过动态流变手段研究了HDPE/EVA和LDPE/EVA两种共混体系的相分离行为,比较了聚乙烯分子结构对共混物相容性的影响。结果表明:对于HDPE/EVA体系,当HDPE质量含量为25%时产生相分离;而LDPE/EVA体系所有组成均未呈现明显相分离。
The phase separation of HDPE/EVA and LDPE/EVA blends was examined using dynamic rheological method,especially the influence of polyethylene molecular structure on the compatibility of the blends.The obtained results showed that for HDPE/EVA blends,the phase separation happened at mass ratio of HDPE=25%.For LDPE/EVA blends,no obvious phase separation in all compositions can be seen.