Precipitation Strengthening by Nanometer-sized Carbides in Hot-rolled Ferritic Steels 被引量:3

Precipitation Strengthening by Nanometer-sized Carbides in Hot-rolled Ferritic Steels
原文传递
导出
摘要 The mechanical properties of the hot-rolled plates of Ti steel and Ti-Mo steel after isothermal transformation in a temperature range of 600 700 ℃ for 60 min have been tested, and the microstructures of the matrix and the characteristics of precipitated nanometer-sized carbides have also been examined by scanning electron microscopy and transmission electron microscopy. The precipitation regularity of nanometer-sized carbides has been studied by thermodynamic method and the contributions of corresponding strengthening mechanisms to the total yield strength have been calculated. The tensile strength of hot-rolled Ti-Mo ferritie steel can achieve 780 MPa with an elongation of 20.0% after being isothermally treated at 600 ℃ for 60 rain, and the tensile strength of Ti steel is 605 MPa with an elongation of 22.7%, according to the results of tensile tests. The critical nucleation size of (Ti,Mo)C is smaller than that of TiC at a given isothermal temperature, but the nucleation rate of (Ti, Mo)C is larger than that of TiC. The grainrefinement strengthening and precipitation strengthening contribute the main amount of the total yield strength. The major increase in yield strength with the decrease of isothermal temperature results from the contribution of precipi tation strengthening. The contribution of precipitation strengthening to the yield strength of the steels has been esti mated. The ferrite phase can be strengthened by about 400 MPa through precipitation strengthening in Ti-Mo steel isothermally treated at 600 ℃ for 60 rain, which is about 200 MPa higher than that of Ti steel under the same conditions. The mechanical properties of the hot-rolled plates of Ti steel and Ti-Mo steel after isothermal transformation in a temperature range of 600 700 ℃ for 60 min have been tested, and the microstructures of the matrix and the characteristics of precipitated nanometer-sized carbides have also been examined by scanning electron microscopy and transmission electron microscopy. The precipitation regularity of nanometer-sized carbides has been studied by thermodynamic method and the contributions of corresponding strengthening mechanisms to the total yield strength have been calculated. The tensile strength of hot-rolled Ti-Mo ferritie steel can achieve 780 MPa with an elongation of 20.0% after being isothermally treated at 600 ℃ for 60 rain, and the tensile strength of Ti steel is 605 MPa with an elongation of 22.7%, according to the results of tensile tests. The critical nucleation size of (Ti,Mo)C is smaller than that of TiC at a given isothermal temperature, but the nucleation rate of (Ti, Mo)C is larger than that of TiC. The grainrefinement strengthening and precipitation strengthening contribute the main amount of the total yield strength. The major increase in yield strength with the decrease of isothermal temperature results from the contribution of precipi tation strengthening. The contribution of precipitation strengthening to the yield strength of the steels has been esti mated. The ferrite phase can be strengthened by about 400 MPa through precipitation strengthening in Ti-Mo steel isothermally treated at 600 ℃ for 60 rain, which is about 200 MPa higher than that of Ti steel under the same conditions.
出处 《Journal of Iron and Steel Research International》 SCIE EI CAS CSCD 2014年第12期1140-1146,共7页
基金 Sponsored by National Natural Science Foundation of China(51271035)
关键词 ferritie steel nanometer sized carbide thermodynamic method precipitation strengthening ferritie steel nanometer sized carbide thermodynamic method precipitation strengthening
  • 相关文献

参考文献23

  • 1Y. Funakawa , T. Shiozaki, K. Tomita, T. Yamamoto, E. Maeda, ISIJ Int. 44 (2004) 1945-195l.
  • 2X. Wang, H. Di, C. Zhang, L. Du, X. Dong, J. Iron Steel Res. Int. 19 (2012) No.6, 64-69.
  • 3H. Yi, L. Du, G. Wang, X. u?, J. Iron Steel Res. Int. 16 (2009) No.4,72-77.
  • 4Y. Shen , C. Wang, X. Sun, Mater. Sci. Eng. A 528 (2011) 8150-8156.
  • 5H. Yi, Z. Liu, G. Wang, D. Wu, J. Iron Steel Res. Int. 17 (2010) No. 12, 54-58.
  • 6A. D. Batte, R. Honeycornbe , Metal Sci. 7 (1973) 160-168.
  • 7R. Okamoto, A. Borgenstam , J. Agren , Acta Mater. 58 (2010) 4783-4790.
  • 8H. Yen, P. Chen, C. Huang, J. Yang, Acta Mater. 59 (2011) 6264-6274.
  • 9S. Mukherjee, 1. B. Timokhina , C. Zhu , S. P. Ringer, P. D. Hodgson, Acta Mater. 61 (2013) 2521-2530.
  • 10J. Cao , Precipitation of Carbonitrides in Nb-Mo-bearing Microalloyed Steels, Kunming University of Science and Tech- no logy , Kunming, 2006.

同被引文献13

引证文献3

二级引证文献9

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部