摘要
用石墨烯修饰碳糊电极,采用循环伏安法在BR缓冲溶液中测定Cu2+的电化学行为。研究了不同条件对Cu2+电化学测定的影响。实验表明,石墨与石墨烯比例为8∶1,pH=3.5,扫描速度为100mV/s进行循环伏安法测定时,在0.136V左右处出现一个峰形较好的特征吸收峰;峰电压与Cu2+浓度在5×10-8~1×10-4 mol/L范围内呈良好的线性关系,相关系数为0.9905,检出限为5.572×10-8 mol/L;连续测定两周,电极表现出较好的稳定性。
Graphene modified carbon paste electrode was used to determine the electrochemical behavior of Cu^2+ in BR buffer solution under different conditions using cyclic voltammetry. As shown by the experimental results, when the proportions of graphite and graphene was 8:1 and the pH value of the buffer solution was 3.5 a well developed characteristic absorption peak was observed at about 0. 136V using cyclic voltammetry at 100mV/s scanning speed; The peak voltage varied linearly with the concentration of Cu^2+ over the range from 5.0×10^-8 to 1.0×10 ^-4mol/L with the correlation coefficient of 0. 9905 and the detection limit of 5. 572 × 10^-8 mol/L; Continuous observation for two weeks showed a high stability of the modified electrode.
出处
《材料科学与工程学报》
CAS
CSCD
北大核心
2014年第4期554-558,共5页
Journal of Materials Science and Engineering
基金
山西省科技攻关基金资助项目(20120321016-01)
煤转化国家重点实验室基金资助项目(J-13-14-909)
关键词
石墨烯
化学修饰电极
循环伏安法
铜离子
graphene
chemically modified electrode
cyclic voltammetry
copper ions