摘要
In order to investigate the carbide dissolution mechanism of high carbon-chromium bearing steel during the intercritical austenitization, the database of TCFE7 of Thermo-calc and MOBFE of DICTRA software were used to calculate the elements diffusion kinetic and the evolution law of volume fraction of carbide. DIL805 A dilatometer was used to simulate the intercritical heat treatment. The microstructure was observed by scanning electron microscopy（SEM）, and the micro-hardness was tested. The experimental results indicate that the dissolution of carbide is composed of two stages： initial austenite growth governed by carbon diffusion which sharply moves up the micro-hardness of quenched martensite, and subsequent growth controlled by diffusion of Cr elements in M3 C. The volume fraction of M3 C decreases with the increasing holding time, and the metallographic analysis shows a great agreement with values calculated by software.
In order to investigate the carbide dissolution mechanism of high carbon-chromium bearing steel during the intercritical austenitization, the database of TCFE7 of Thermo-calc and MOBFE of DICTRA software were used to calculate the elements diffusion kinetic and the evolution law of volume fraction of carbide. DIL805 A dilatometer was used to simulate the intercritical heat treatment. The microstructure was observed by scanning electron microscopy（SEM）, and the micro-hardness was tested. The experimental results indicate that the dissolution of carbide is composed of two stages： initial austenite growth governed by carbon diffusion which sharply moves up the micro-hardness of quenched martensite, and subsequent growth controlled by diffusion of Cr elements in M3 C. The volume fraction of M3 C decreases with the increasing holding time, and the metallographic analysis shows a great agreement with values calculated by software.
基金
Funded by the National High-tech Research and Development Program of China(863 Program)