钻杆螺纹部位疲劳损伤的磁记忆检测试验研究

Experimental Study on Fatigue Damage of the Drilling Pipe Thread Based on Metal Magnetic Memory Testing
下载PDF
导出
摘要 钻杆在使用过程中由于工况恶劣,受力情况复杂,其螺纹部位极易发生疲劳失效,造成重大损失。笔者利用磁记忆检测的基本原理,对不同使用工况的钻杆螺纹部位的疲劳损伤情况进行了现场检测试验,验证了磁记忆检测技术在检测钻杆螺纹疲劳损伤状况方面的可用性,证实了螺纹容易发生疲劳损伤的部位位于密封面端起前三扣位置,同时证实随着使用时间的延长,钻杆螺纹部位疲劳损伤越严重,并且在对大量检测数据进行分析的基础上建立了钻杆螺纹分级推荐标准。 The thread of drilling pipes can easily generate fatigue failure and cause heavy losses because of bad working condition and complicated stresses in drilling process.Field examinations of the fatigue failure of the drill pipe thread in different operating conditions were carried out based on the theory of MMMT (Metal Magnetic Memory Testing).The field examinations verified that MMMT is useful in examination of the fatigue failure of the drill pipe,and it is the first three threads from the sealing face that can easily generate fatigue failure,and the longer time the drill pipes are used,the more serious fatigue damage condition of the drill pipe thread will happen.And the recommended standard of the drill pipe thread classification is established based on the analysis of a large number of inspection data.
出处 《华北科技学院学报》 2014年第11期24-29,共6页 Journal of North China Institute of Science and Technology
基金 中国石油天然气股份有限公司塔里木油田分公司科研项目"钻柱疲劳损伤一体化监控技术推广应用"(201013100220)
关键词 钻杆螺纹 磁记忆 疲劳损伤 检测 drill pipe thread metal magnetic memory fatigue damage detection
  • 相关文献

参考文献8

二级参考文献62

共引文献203

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部