This work aimed at effectively utilizing the chemically depolymerized waste poly（ethylene terephthalate）（PET） fibers into useful products for the textile industry.PET fibers were glycolytically degraded by excess ethylene glycol as depolymerizing agent and zinc acetate dihydrate as catalyst.The glycolysis product,bis（2-hydroxyethyl） terephthalate（BHET）,was purified through repeated crystallization to get an average yield above 80%.Then,BHET was nitrated,reduced,and azotized to get diazonium salt.Finally,the produced diazonium salt was coupled with 1-（4-sulfophenyl）-3-methyl-5-pyrazolone to get azo dyestuff.The structures of BHET and azo dyestuff were identified by FT1 R and ^1H NMR spectra and elemental analysis.Nylon filaments dyed by the synthesized azo dyestuff with the dye bath pH from 4.14 to 5.88 showed bright yellow color.The performances of the dyestuff were described with dye uptake,color fastness,K/S,L^＊,a^＊,b^＊.and △E^＊ values.
This work aimed at effectively utilizing the chemically depolymerized waste poly（ethylene terephthalate）（PET） fibers into useful products for the textile industry.PET fibers were glycolytically degraded by excess ethylene glycol as depolymerizing agent and zinc acetate dihydrate as catalyst.The glycolysis product,bis（2-hydroxyethyl） terephthalate（BHET）,was purified through repeated crystallization to get an average yield above 80%.Then,BHET was nitrated,reduced,and azotized to get diazonium salt.Finally,the produced diazonium salt was coupled with 1-（4-sulfophenyl）-3-methyl-5-pyrazolone to get azo dyestuff.The structures of BHET and azo dyestuff were identified by FT1 R and ^1H NMR spectra and elemental analysis.Nylon filaments dyed by the synthesized azo dyestuff with the dye bath pH from 4.14 to 5.88 showed bright yellow color.The performances of the dyestuff were described with dye uptake,color fastness,K/S,L^＊,a^＊,b^＊.and △E^＊ values.
基金
financially supported by the National High-tech R&D Program of China(863 Program,No.2012AA030313)
the Open Project Program of Key Laboratory of Eco-Textiles(Jiangnan University),Ministry of Education,China(No.KLET1115)
the Fundamental Research Funds for the Central Universities(No. JUSRP11201)
the Cooperative Innovation Fund-Prospective Project of Jiangsu Province,China(No.BY2012060)