Fracture toughness and fracture behavior of SA508-Ⅲ steel at different temperatures 被引量:2

Fracture toughness and fracture behavior of SA508-Ⅲ steel at different temperatures
下载PDF
导出
摘要 The fracture toughness of SA508-Ⅲ steel was studied in the temperature range from room temperature to 320℃ using the J-integral method. The fracture behavior of the steel was also investigated. It was found that the conditional fracture toughness (JQ) of the steel first decreased and then increased with increasing test temperature. The maximum and minimum values of do were 517.4 kJ/m^2 at 25℃ and 304.5 kJ/m^2 at 180℃, respectively. Dynamic strain aging (DSA) was also observed to occur when the temperature exceeded 260℃ with a certain strain rate. Both the dislocation density and the number of small dislocation cells effectively increased because of the occurrence of DSA; as a consequence, crack propagation was more strongly inhibited in the steel. Simultaneously, an increasing number of fine carbides precipitated under high stress at temperatures greater than 260℃. Thus, the deformation resistance of the steel was improved and the Jo was enhanced. The fracture toughness of SA508-Ⅲ steel was studied in the temperature range from room temperature to 320℃ using the J-integral method. The fracture behavior of the steel was also investigated. It was found that the conditional fracture toughness (JQ) of the steel first decreased and then increased with increasing test temperature. The maximum and minimum values of do were 517.4 kJ/m^2 at 25℃ and 304.5 kJ/m^2 at 180℃, respectively. Dynamic strain aging (DSA) was also observed to occur when the temperature exceeded 260℃ with a certain strain rate. Both the dislocation density and the number of small dislocation cells effectively increased because of the occurrence of DSA; as a consequence, crack propagation was more strongly inhibited in the steel. Simultaneously, an increasing number of fine carbides precipitated under high stress at temperatures greater than 260℃. Thus, the deformation resistance of the steel was improved and the Jo was enhanced.
出处 《International Journal of Minerals,Metallurgy and Materials》 SCIE EI CAS CSCD 2014年第12期1187-1195,共9页 矿物冶金与材料学报(英文版)
基金 financially supported by the Major State Basic Research Development Program of China (No. 2011CB610506) the National Natural Science Foundation of China (Nos. 51371044 and 51171039) the Fundamental Research Fund for the Central Universities of China (No. N130410001)
关键词 low alloyed steel fracture toughness fracture behavior TEMPERATURE dynamic strain aging nuclear power plants low alloyed steel fracture toughness fracture behavior temperature dynamic strain aging nuclear power plants
  • 相关文献

参考文献5

二级参考文献71

  • 1P.Diano, A.Muggeo, J.C.Van Duysen, M.Guttmann, Relationship between microstructure and mechanical properties of Alloy 690 tubes for steam generators, Journal of Nuclear Materials, 168(3), 290(1989).
  • 2GAO X.S., B.A.Yong, T.S.Srivatsan, J.P.King, The response of alloy 690 tubing in a pressurized water reactor environment, Materials and Design, 28(2), 373(2007).
  • 3K.Stiller, J.O.Nilsson, K.Norring, Structure, chemistry, and stress corrosion cracking of grain boundaries in alloys 600 and 690, Metallurgical and Materials Transactions A, 27A(2), 327(1996).
  • 4Seong Sik Hwang, Hong Pyo Kim, Yun Soo Lim, Joung Soo Kim, L.Thomas, Transgranular SCC mechanism of thermally treated alloy 600 in alkaline water containing lead, Corrosion Science, 49(10), 3797(2007).
  • 5R.A.Page, A.Mcminn, Relative stress corrosion susceptibilities of alloys 690 and 600 in simulated boiling water reactor environments, Metallurgical Transactions A, 1TA(5), 877(1986).
  • 6C.M.Brown, W.J.Mills, Fracture toughness of alloy 690 and EN52 welds in air and water, Metallurgical and Materials Transactions A, 33A(6), 1725(2002).
  • 7D.M.Symons, Effect of carbide precipitation on the hydrogen-enhanced fracture behavior of alloy 690, Metallurgical and Materials Transactions A, 29A(4), 1265(1998).
  • 8Venkatesh Vasisht, H.J.Rack, Elevated temperature hardening of INCONEL 690, Mechanics of Materials, 30(1), 69(1998).
  • 9H.B.Park, Y.H.Kim, B.W.Lee, K.S.Rheem, Effect of heat treatment on fatigue crack growth rate of Inconel 690 and Inconel 600, Journal of Nuclear Materials, 231(3), 204(1996).
  • 10I.A.Choudhury, M.A.EI-Baradie, Machinability of nickelbase super alloys: A general review, Journal of Materials Processing Technology, 77(1-3), 278(1998).

共引文献17

同被引文献11

引证文献2

二级引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部