摘要
To extract vanadium in an environment friendly manner, this study focuses on the process of leaching vanadium from vanadium slag by high pressure oxidative acid leaching. Characterizations of the raw slag, mineralogy transformation, and the form of leach residues were made by X-ray diffraction, scanning electron microscopy, and energy dispersive X-ray spectroscopy. The result shows that the vana-dium slag is composed of major phases of fayalite, titanomagnetite, and spinel. During the high pressure oxidative acid leaching process, the fayalite and spinel phases are gradually decomposed by sulfuric acid, causing the release of vanadium and iron in the solution. Meanwhile, unreacted silicon and titanium are enriched in the leach residues. With the initial concentration of sulfuric acid at 250 g·L^-1, a leaching tem-perature of 140℃, a leaching time of 50 min, a liquid-solid ratio of 10：1 mL·g^-1, and oxygen pressure at 0.2 MPa, the leaching rate of vana-dium reaches 97.69%.
To extract vanadium in an environment friendly manner, this study focuses on the process of leaching vanadium from vanadium slag by high pressure oxidative acid leaching. Characterizations of the raw slag, mineralogy transformation, and the form of leach residues were made by X-ray diffraction, scanning electron microscopy, and energy dispersive X-ray spectroscopy. The result shows that the vana-dium slag is composed of major phases of fayalite, titanomagnetite, and spinel. During the high pressure oxidative acid leaching process, the fayalite and spinel phases are gradually decomposed by sulfuric acid, causing the release of vanadium and iron in the solution. Meanwhile, unreacted silicon and titanium are enriched in the leach residues. With the initial concentration of sulfuric acid at 250 g·L^-1, a leaching tem-perature of 140℃, a leaching time of 50 min, a liquid-solid ratio of 10：1 mL·g^-1, and oxygen pressure at 0.2 MPa, the leaching rate of vana-dium reaches 97.69%.
基金
supported by the National High Technology Research and Development Program of China(No.2012AA062303)
the National Natural Science Foundation of China(Nos.U1202274,51004033,and 51204040)
the Doctoral Fund Project of China(No. 20120042110011)