Microstructure and corrosion behaviour of gas tungsten arc welds of maraging steel

Microstructure and corrosion behaviour of gas tungsten arc welds of maraging steel
下载PDF
导出
摘要 Superior properties of maraging steels make them suitable for the fabrication of components used for military applications like missile covering, rocket motor casing and ship hulls. Welding is the main process for fabrication of these components, while the maraging steels can be fusion welded using gas tungsten arc welding(GTAW) process. All these fabricated components require longer storage life and a major problem in welds is susceptible to stress corrosion cracking(SCC). The present study is aimed at studying the SCC behaviour of MDN 250(18% Ni) steel and its welds with respect to microstructural changes. In the present study, 5.2 mm thick sheets made of MDN 250 steel in the solution annealed condition was welded using GTAW process. Post-weld heat treatments of direct ageing(480 C for 3 h), solutionizing(815 C for 1 h) followed by ageing and homogenizing(1150 C for 1 h) followed by ageing were carried out. A mixture of martensite and austenite was observed in the microstructure of the fusion zone of solutionized and direct aged welds and only martensite in as-welded condition. Homogenization and ageing treatment have eliminated reverted austenite and elemental segregation. Homogenized welds also exhibited a marginal improvement in the corrosion resistance compared to those in the as-welded, solutionized and aged condition. Constant load SCC test data clearly revealed that the failure time of homogenized weld is much longer compared to other post weld treatments, and the homogenization treatment is recommended to improve the SCC life of GTA welds of MDN 250 Maraging steel. Superior properties of maraging steels make them suitable for the fabrication of components used for military applications like missile covering, rocket motor casing and ship hulls. Welding is the main process for fabrication of these components, while the maraging steels can be fusion welded using gas tungsten arc welding (GTAW) process. All these fabricated components require longer storage life and a major problem in welds is susceptible to stress corrosion cracking (SCC). The present study is aimed at studying the SCC behaviour of MDN 250 (18%Ni) steel and its welds with respect to microstructural changes. In the present study, 5.2 mm thick sheets made of MDN 250 steel in the solution annealed condition was welded using GTAW process. Post-weld heat treatments of direct ageing (480 ?C for 3 h), solutionizing (815 ?C for 1 h) followed by ageing and homogenizing (1150 ?C for 1 h) followed by ageing were carried out. A mixture of martensite and austenite was observed in the microstructure of the fusion zone of solutionized and direct aged welds and only martensite in as-welded condition. Homogenization and ageing treatment have eliminated reverted austenite and elemental segregation. Homogenized welds also exhibited a marginal improvement in the corrosion resistance compared to those in the as-welded, solutionized and aged condition. Constant load SCC test data clearly revealed that the failure time of homogenized weld is much longer compared to other post weld treatments, and the homogenization treatment is recommended to improve the SCC life of GTA welds of MDN 250 Maraging steel.
出处 《Defence Technology(防务技术)》 SCIE EI CAS CSCD 2015年第1期48-55,共8页 Defence Technology
基金 Financial assistance from Defence Research Development Organization (DRDO)
关键词 18% Ni maraging steel GAS TUNGSTEN ARC welding Post weld heat TREATMENT Solutionising Ageing TREATMENT PITTING corrosion Stress corrosioncracking (SCC) 18% Ni maraging steel Gas tungsten arc welding Post weld heat treatment Solutionising Ageing treatment Pitting corrosion Stress corrosion cracking(SCC)
  • 相关文献

参考文献19

  • 1Garrison Jr WM. Ultrahigh-strength steels for aerospace applications.JOM 1990;42(5):20-4.
  • 2Tomita Y. Development of fracture toughness of ultrahigh strength lowalloy steels for aircraft and aerospace applications. Mat Sci Technol1991:481.
  • 3Olson GB. Overview: science of steel, innovations in ultrahigh strengthsteel techno-logy. In: Proceedings of the 34th Sagamore Army MaterialsResearch Conference; 1987. p 3.
  • 4Floreen S, Decker RF. Source book on maraging steels, ASM, OH. 1979-20.
  • 5Decker RF, Floreen S. Maraging steels: recent developments and applications.Warrendale, PA: TMS-AIME; 1988-1.
  • 6Vasudevan VK, Kim SJ, Wayman CM. Precipitation reactions andstrengthening mechanisms in maraging steels. Metall Trans A1990;21(10):2655-88.
  • 7Gilmour JB. Environmental cracking of 18 Ni 200 maraging steel.Corrosion 1977;33(10):357-63.
  • 8Syrett BC. Stress corrosion cracking in 18% Ni (250) maraging steel.Corrosion 1971:270-80.
  • 9Diwakar V, Arumugam S, Lakshmanan TS, Sarkar BK. Environmentalstress intensity for maraging steel J. Mater Sci 1986;21(6):1927e31.
  • 10Jha AK, Reddy KG, John KM, Ramesh Narayanan P, Natarajan A,Lakshmanan TS. Pract Metallogr 1994:144.

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部