10^#碳钢在NH4HS溶液中的冲蚀规律 被引量:11

Erosion-Corrosion Behaviors of 10^# Carbon Steel in NH4HS Solution
下载PDF
导出
摘要 设计搭建旋转式冲蚀实验装置,采用电化学方法,针对含硫污水腐蚀体系,考察了NH4HS质量分数、介质温度、Cl-质量浓度等对典型加氢空冷器管材10#碳钢冲刷腐蚀规律的影响;结合扫描电镜(SEM)分析腐蚀产物膜形貌,揭示10#碳钢发生腐蚀的内在机制。结果表明,在质量分数5.0%NH4HS溶液中,10#碳钢表面形成致密的腐蚀产物膜;随着NH4HS质量分数的增加,腐蚀产物膜厚度增加,但出现的龟裂和疏松现象,降低了对金属基体的保护作用;随着介质温度的升高,腐蚀产物膜致密度下降,易发生脱落;腐蚀产物膜受Cl-侵蚀会成蜂窝状,流速大于3.5m/s时,10#碳钢的腐蚀速率随Cl-质量浓度的增加而迅速升高。 The erosion-corrosion rotary experiment device was designed and built to research the erosion-corrosion rules of 10^#carbon steel,which was commonly used in the reactor effluent air cooler(REAC).Based on the electrochemical test and scanning electron microscope(SEM),the erosion-corrosion rate of 10^#carbon steel and the morphology of corrosion product were analyzed by considering the NH4 HS mass fraction,system temperature and chlorine ion mass concentration.The results showed that the dense corrosion product film was formed on the surface of 10^#carbon steel when it was in 5.0%NH4HS solution,and with the increase of NH4 HS mass fraction the thickness of the product film increased,however,the film would become loose and cracked,which reduced its protective effect to metal base.The density of the corrosion product film decreased with the temperature rising and the shedding phenomenon finally occurred.The honeycomb morphology of product film appeared due to the chloride ion penetration.When the velocity of NH4 HS solution was more than 3.5m/s,the corrosion rate of 10^#carbon steel increased rapidly with the increase of chloride ion mass concentration in solution.
出处 《石油学报(石油加工)》 EI CAS CSCD 北大核心 2014年第5期928-933,共6页 Acta Petrolei Sinica(Petroleum Processing Section)
基金 国家科技支撑计划项目(2012BAK13B03-02) 国家基金委与神华集团联合资助项目(U1261124) 浙江理工大学科研启动基金项目(1202825-Y)资助
关键词 10^#碳钢 NH4HS溶液 冲蚀 电化学测试 腐蚀形貌 10^# carbon steel NH4HS solution erosion-corrosion electrochemical test corrosion morphology
  • 相关文献

参考文献14

  • 1李立权.提高我国加氢裂化工程技术的对策思考[J].石油学报(石油加工),2010,26(S1):51-58. 被引量:5
  • 2SHAMMERI H A, MUKHOPADHYAY P K, RADHAKRISHNAN R. Preventing ammonium salt corrosion in high pressure flash gas lines[C]//NACE International. Corrosion 2010. Houston : NACE International Publications Division, 2010: 10356.
  • 3KANE R D, HORVATH R J, CAYARD M S. Major improvements in reactor effluent air cooler reliability [J].Hydrocarbon Processing, 2006, 85(9): 99-111.
  • 4KAZUHIRO T, KOJI K, KOJI Y, et al. The application of process analyses to prevent corrosion in sour water stripper overhead cooler tubes[C]//NACE International. Corrosion 2005. Houston: NACE International Publications Division, 2005: 05569.
  • 5PANDEY R K. Failure analysis of refinery tubes of overhead condenser[J]. Engineering Failure Analysis, 2006, 13(5): 739-746.
  • 6华贲.低碳经济时代的中国炼油工业[J].石油学报(石油加工),2010,26(6):835-840. 被引量:9
  • 7API RP 932-A-2004. A study of corrosion in hydroprocessing reactor effluent air cooler system[S].2004.
  • 8RICHARD J H, MICHAEL S C, RUSSELL D K. Prediction and assessment of ammonium bisulfide corrosion under refinery sour water service conditions [C]//NACE International. Corrosion 2006. Houston: NACE International Publications Division, 2006: 06576.
  • 9ANWAR U H,HANI M T. Corrosion of carbon steel caustic header in the presence of chloride ions[J]. Engineering Failure Analysis, 2009, 16(3) : 825-832.
  • 10YABUKI A, MURAKAMI M. Breakaway properties of film formed on copper and copper alloys in erosion- corrosion by mass transfer equation [J]. Materials and Corrosion, 2008, 59(1): 25-31.

二级参考文献29

  • 1刘兴山,陈岩.加氢裂化反应加热炉炉管开裂原因及对策[J].石油化工设计,2006,23(2):19-21. 被引量:3
  • 2华贲,熊标.加速开发中国LNG汽车产业链[J].中外能源,2007,12(1):12-15. 被引量:12
  • 3吴国干.非常规天然气正改变世界能源格局[EB/OL].中国能源网,2010-05-28.http://www.china5e.com/show.php?contentid=101804.
  • 4MIT Energy Initiative. The Future of Natural Gas, an interdisciplinary Study.
  • 5中美合作非常规天然气开发 业界期待政策[EB/OL].2010-06-01.
  • 6SMITH B.LNGV在亚洲和世界的发展[D].2010广州天然气峰会,2010.
  • 7华贲.中国分布式能源发展机制创新的历史机遇.中国电业 技术版,2010,1(2):37-40.
  • 8齐树柏.重油高效利用加工过程中异常腐蚀的调查报告[C].日本石油产业活化中心,1990.3..
  • 9Piehl R. Survey of corrosion in hydrocracker effluent air coolers[J]. Materials Performance, 1976, 15(1): 15 - 20
  • 10Harvey C, Singh A. Mitigate failures for reactor effluent air coolers[J]. Hydrocarbon Processing, October, 1999:59 - 72

共引文献49

同被引文献48

引证文献11

二级引证文献10

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部