固溶处理工艺对改良铸造铝硅合金组织和性能的影响 被引量:4

Effect of Solution Treatment Process on the Microstructure and Property of Modified Aluminum Silicon Casting Alloy
下载PDF
导出
摘要 通过不同温度和时间的固溶制度研究了固溶处理工艺对改良铸造铝硅合金(0.35%Mg,7.0%Si,0.2%Ni,2.0%Cu,0.8%RE,0.2%Mn,0.1%V,其余为铝)组织和性能的影响。实验结果表明,在495℃×5h进行固溶处理时,改良铸造铝硅合金具有最好的综合力学性能:Rm=239MPa,硬度=103HBS,A=6.24%;改良铸造铝硅合金于495℃×5h固溶淬火析出富含Si、Cu、Ni以及RE元素的Si、Al Cu、Al6Cu3Ni、Alx Cu Ce相。这些相的存在,有利于提高合金的力学性能和高温性能。合金经过热处理后以韧性断裂为主要方式并伴有准解理面现象,拉伸断口微观形貌主要表现为韧窝断口特征,有些存在少量撕裂棱。 By aid of solution system with different temperature and time, effect of solution treatment process on the microstructure and mechanical properties of modified aluminium silicon casting alloy(0.35% Mg,7.0% Si,0.2% Ni,2.0% Cu,0.8% RE,0.2% Mn,0.1% V,balance is Al)was studied. The results show that,at 495℃×5h for solution treatment,modified aluminium silicon casting alloy has the best comprehensive mechanical properties:б=239MPa,HBS=103HBS,β=6.24%;modified aluminium silicon casting alloy at 495℃×5h after solution quench had Si,Al Cu,Al6Cu3 Ni,Alx Cu Ce phases containing rich Si,Cu,Ni and RE elements. These phases were helpful to improve the mechanical properties and high temperature performance of alloy. Ductile fracture for alloy after heat treatment is the main way and is accompanied by the quasi cleavage phenomenon. The tensile fracture morphology is mainly dimple fracture characteristics, some of the presence of a small amount of tear ridges.
出处 《铝加工》 CAS 2015年第1期25-29,共5页 Aluminium Fabrication
基金 广西大学有色金属及材料加工新技术教育部重点实验室开放基金(合同编号:GXKFJ-01)
关键词 固溶处理 改良铸造铝硅合金 热处理 韧性断裂 solution treatment modified Al-Si casting alloy heat treatment ductile fracture
  • 相关文献

参考文献2

二级参考文献18

  • 1宁爱林,刘志义,郑青春,曾苏民.分级固溶对7A04铝合金组织与性能的影响[J].中国有色金属学报,2004,14(7):1211-1216. 被引量:27
  • 2Engler O,Sachot E,Ehrstrom J C.Recrystallisation and texture in hot deformed aluminium alloy 7010 thick plates[J].Materials Science and Technology,1996,12:717-729.
  • 3Robson J D.Optimizing the homogeniztion of Zirconium containing commercial aluminium alloys using a novel process model[J].Materials Science and Engineering A,2002,338:219-229.
  • 4Robson J D,Prangnell P B.Predicting the recrystallized volume fraction in AA7050 hot rolled plate[J].Materials Science and Technology,2002,18(6):607 -619.
  • 5Chen Kanghua,Liu Hongwei,Zhang Zhuo,et al.The improvement of constituent dissolution and mechanical properties of 7055 aluminum alloy by stepped heat treatments[J].Journal of Materials Processing Technology,2003,142:190-196.
  • 6Bryant A J,Thomas A T.The relationship between grain structure and quench-sensitivity of an extruded Al-Zn-Mg alloy[J].Journal of the Institute of Metals,1972,100:40-44.
  • 7Yamazaki S,Otsuka H,Kikuchi T.Peripheral-recrystallized structures formed in Al-Zn-Mg-Cu-Zr alloy materials during extrusion and their quenching sensitivity[J].Journal of Materials Processing Technology,1993,38(4):689-701.
  • 8Zakharov V V,Novikov Ⅱ,Elagin Ⅵ,et al.Decomposition of the solid solution in unrecyrstallized plates of AlZnMgMnZr alloy[J].Metallov i Term Obrab Metal,1970,5:70-73.
  • 9Fjeldly H,Roven J,Rauch E.Strain localization in solution heat treated Al-Zn-Mg alloy[J].Materials Science and Engineering A,2001,380:165-170.
  • 10Park B K,Vruggink J E.Properties and microstructure of intermediate thermal-mechanihal treated 7475-T6 sheet[J].Thermal-mechanical Processing of Aluminum Alloys,AIME,1979,25-49.

共引文献53

同被引文献24

引证文献4

二级引证文献8

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部