In this study, the effects of Zr-Ti combined deoxidation and AI deoxidation on the impact toughness of coarse- grained heat-affected zone in high-strength low-alloy steels were investigated. More fine oxides were formed in the Zr-Ti-killed steel than in Al-killed steel. It was also found that more acicular ferrite grains were formed in the coarse-grained heat-affected zone in the Zr-Ti-killed steel than in Al-killed steel. The impact toughness of coarse-grained heat-affected zone of Zr-Ti-kiUed steel was higher than that of Al-killed steel. The good impact toughness was attributable to the pinning effect of fine oxides and the formation of acicular ferrite grains on fine oxides.
In this study, the effects of Zr-Ti combined deoxidation and AI deoxidation on the impact toughness of coarse- grained heat-affected zone in high-strength low-alloy steels were investigated. More fine oxides were formed in the Zr-Ti-killed steel than in Al-killed steel. It was also found that more acicular ferrite grains were formed in the coarse-grained heat-affected zone in the Zr-Ti-killed steel than in Al-killed steel. The impact toughness of coarse-grained heat-affected zone of Zr-Ti-kiUed steel was higher than that of Al-killed steel. The good impact toughness was attributable to the pinning effect of fine oxides and the formation of acicular ferrite grains on fine oxides.
基金
This work was supported by the China Postdoctoral Science Foundation C Grant No. 2014M550414 ） and the National Natural Science Foundation of China （ Grant No. 51401152）.