Nanocrystalline copper-cobalt ferrites with composition Cu_（1-x）Co_xFe_2O_4,where x = 0.2 and 0.8,were synthesized by mechanochemical treatment of co-precipitated precursors.The ferrite powders were characterized by XRD and Mossbauer spectroscopy.Results proved obtaining of spinel ferrites with crystallite size smaller than 10 nm.Increasing of crystallite size of samples with increasing of mechanochemical treatment duration was established,too.Catalytic properties of obtained ferrites were tested in reactions of oxidation of CO,methanol and dimethyl ether.High catalytic activity of nanocrystalline copper-cobalt ferrites toward CO and CH_3OH（about 100% conversions of CO and CH_3OH at 160 ℃）and moderate activity toward（CH_3）_2O oxidation were established.The results obtained revealed that the Co/Cu atomic ratio is an important factor determinant the behavior of catalysts toward methanol and DME oxidation.
Nanocrystalline copper-cobalt ferrites with composition Cu_（1-x）Co_xFe_2O_4,where x = 0.2 and 0.8,were synthesized by mechanochemical treatment of co-precipitated precursors.The ferrite powders were characterized by XRD and Mossbauer spectroscopy.Results proved obtaining of spinel ferrites with crystallite size smaller than 10 nm.Increasing of crystallite size of samples with increasing of mechanochemical treatment duration was established,too.Catalytic properties of obtained ferrites were tested in reactions of oxidation of CO,methanol and dimethyl ether.High catalytic activity of nanocrystalline copper-cobalt ferrites toward CO and CH_3OH（about 100% conversions of CO and CH_3OH at 160 ℃）and moderate activity toward（CH_3）_2O oxidation were established.The results obtained revealed that the Co/Cu atomic ratio is an important factor determinant the behavior of catalysts toward methanol and DME oxidation.
基金
sponsored by the Bulgarian National Science Fund under Project DDVU 02/07/2010
financial support by the European Social Fund within the framework of Operating Program "Development of Human Resources"(BG051PO001-3.3.06-0050)